1.1These test methods cover the determination of the modulus of rupture in bending of glass and glass-ceramics.
1.2These test methods are applicable to annealed and prestressed glasses and glass-ceramics available in varied forms. Alternative test methods are described; the test method used shall be determined by the purpose of the test and geometric characteristics of specimens representative of the material.
1.2.1Test Method A is a test for modulus of rupture of flat glass.
1.2.2Test Method B is a comparative test for modulus of rupture of glass and glass-ceramics.
1.3The test methods appear in the following order:
| | Sections |
| Test Method A | 6 to 9 |
| Test Method B | 10 to 15 |
1.4This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific hazard statements are given in Section 10 and A1.5, A2.3.3, A2.4.3 and A2.5.3.
1.5This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.