ASTM A 1091/A1091M : 2024

1.1This specification covers creep-strength enhanced alloy steel castings for valves, flanges, fittings, and other pressure-containing parts intended primarily for high-temperature service (see Note 1). However, they are not restricted to such applications and the castings may be used for other applications for which the attributes of the material, as defined by this specification, are suitable.

1.2Two grades of martensitic alloy steel, Grade C91 (UNS No. J84090) and Grade C933 (UNS No. J84093), are covered. Grade C91 is provided in two classes, differentiated by the type of heat treatment after welding. Both grades, and similar steels, are characterized by a predominantly tempered martensitic or tempered bainitic microstructure that is stabilized by the precipitation of temper-resistant particles at various precipitate nucleation sites in the microstructure. Such steels are designed to have creep-rupture strengths significantly superior to those of alloys of nominally similar compositions, but in which the precipitates or nucleation sites are absent. Since this crucial difference cannot be revealed by room temperature mechanical property tests, these alloys require tighter controls on manufacturing and processing.

1.3The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.

1.4This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.