ASTM A 710/A710M : 2025 : REDLINE

1.1This specification covers low-carbon precipitation-strengthened nickel-copper-chromium-molybdenum-columbium (niobium) alloy steel plates for general applications. The alloys in this specification are strengthened by precipitation in various temperature ranges. Precipitation strengthening can occur upon air cooling after hot rolling, during normalizing, and by another heat treatment. These grades are not intended for use in applications above 900 °F [480 °C].

1.2Two grades, each with three classes, are provided as follows:

1.3Grade A provides minimum yield strength levels ranging from 50 ksi to 85 ksi [345 MPa to 585 MPa], depending on thickness and condition.

1.4Grade A, Class 1, plates are limited to a maximum thickness of ³/₄in. [20 mm]. The maximum thickness of Grade A, Classes 2 and 3, is limited only by the capacity of the composition to meet the specified mechanical property requirements; however, current practice normally limits the maximum thickness to 8 in. [200 mm].

1.5Mandatory notch toughness requirements are specified for Grade A, Class 1.

1.6Grade B provides minimum yield strength levels ranging from 70 ksi to 75 ksi [485 MPa to 515 MPa], depending on thickness and condition.

1.7Grade B plates are limited to a maximum thickness of 2 in. [50 mm].

1.8Mandatory notch toughness requirements are specified for the three classes of Grade B.

1.9When the steel is to be welded, it is presupposed that a welding procedure suitable for the grade of steel and intended use or service will be utilized. See Appendix X3 of Specification A6/A6M for information on weldability.

1.10The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.

1.11This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.