ASTM A 736/A736M : 2017
Current
The latest, up-to-date edition.
Standard Specification for Pressure Vessel Plates, Low-Carbon Age-Hardening Nickel-Copper-Chromium-Molybdenum-Columbium (Niobium) Alloy Steel
Hardcopy , PDF
English
01-11-2017
Important note : Users cannot be edited or removed once added to your Multi user PDF.| Committee |
A 01
|
| DocumentType |
Standard
|
| Pages |
3
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Current
|
| Supersedes |
1.1This specification2 covers low-carbon age-hardening alloy steel plates for welded pressure vessels and piping components. The specification covers nickel-copper-chromium-molybdenum-columbium (niobium) steel.
1.2Plates under this specification are available as follows:
1.2.1Available in Grade A, Class 3 only.
1.2.1.1Quenched and precipitation heat treated with a minimum specified tensile strength of 85 ksi for thinner plates and 75 and 70 ksi for thicker plates, with the minimum tensile strength dependent upon the plate thickness. The maximum thickness of Grade A, Class 3 plates is limited only by the capacity of the chemical composition and heat treatment to meet the specified mechanical property requirements.
1.3This specification is expressed in both inch-pound units and in SI units. However, unless the order specifies the applicable “M” specification designation (SI units), the material shall be furnished in inch-pound units.
1.4The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents. Therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with this specification.
1.5This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
| ASTM A 577/A577M : 2017 : R2023 | Standard Specification for Ultrasonic Angle-Beam Examination of Steel Plates |
| ASTM A 577/A577M : 2017 | Standard Specification for Ultrasonic Angle-Beam Examination of Steel Plates |
| ASTM A 578/A578M : 2017 : R2023 | Standard Specification for Straight-Beam Ultrasonic Examination of Rolled Steel Plates for Special Applications |
| ASTM A 20/A20M : 2004 | Standard Specification for General Requirements for Steel Plates for Pressure Vessels |
| ASTM A 577/A577M : 1990 : R1996 | Standard Specification for Ultrasonic Angle-Beam Examination of Steel Plates |
| ASTM A 578/A578M : 2017 | Standard Specification for Straight-Beam Ultrasonic Examination of Rolled Steel Plates for Special Applications |
| ASTM A 435/A435M : 2017 | Standard Specification for Straight-Beam Ultrasonic Examination of Steel Plates |
| ASTM A 578/A578M : 1996 | Standard Specification for Straight-Beam Ultrasonic Examination of Plain and Clad Steel Plates for Special Applications |
| ASTM A 435/A435M : 2017 : R2023 | Standard Specification for Straight-Beam Ultrasonic Examination of Steel Plates |
| ASTM A 20/A20M : 2000 : REV B | Standard Specification for General Requirements for Steel Plates for Pressure Vessels |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.