ASTM B 580 : 1979 : R2019
Current
The latest, up-to-date edition.
Standard Specification for Anodic Oxide Coatings on Aluminum
Hardcopy , PDF
English
01-04-2019
Important note : Users cannot be edited or removed once added to your Multi user PDF.| Committee |
B 08
|
| DocumentType |
Standard
|
| Pages |
3
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Current
|
| Supersedes |
1.1This specification covers requirements for electrolytically formed porous oxide coatings on aluminum and aluminum alloy parts in which appearance, abrasion resistance, electrical properties, and protection against corrosion are important. Nonporous, barrier layer anodic coatings used for electrical capacitors are not covered. Seven types of coatings as shown in Table 1 are provided. Definitions and typical examples of service conditions are provided in Appendix X1.
Note 1:It is recognized that uses exist in which modifications of the coatings covered by this specification may be required. In such cases the particular properties desired by the purchaser should be the subject of agreement between the purchaser and the manufacturer.
1.2The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.3This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
| ASTM B 244 : 2009 : R2014 | Standard Test Method for Measurement of Thickness of Anodic Coatings on Aluminum and of Other Nonconductive Coatings on Nonmagnetic Basis Metals with Eddy-Current Instruments |
| ASTM B 368 : 2009 : R2014 | Standard Test Method for Copper-Accelerated Acetic Acid-Salt Spray (Fog) Testing (CASS Test) |
| ASTM B 457 : 1967 : R2018 | Standard Test Method for Measurement of Impedance of Anodic Coatings on Aluminum (Withdrawn 2023) |
| ASTM E 430 : 2019 | Standard Test Methods for Measurement of Gloss of High-Gloss Surfaces by Abridged Goniophotometry |
| ASTM E 430 : 2023 | Standard Test Methods for Measurement of Gloss of High-Gloss Surfaces by Abridged Goniophotometry |
| ASTM B 136 : 1984 : R2018 | Standard Method for Measurement of Stain Resistance of Anodic Coatings on Aluminum |
| ASTM B 602 : 1988 : R2016 | Standard Test Method for Attribute Sampling of Metallic and Inorganic Coatings |
| ASTM B 602 : 2021 | Standard Guide for Attribute Sampling of Metallic and Inorganic Coatings |
| ASTM B 137 : 1995 : R2021 | Standard Test Method for Measurement of Coating Mass Per Unit Area on Anodically Coated Aluminum |
| ASTM B 117 : 2019 | Standard Practice for Operating Salt Spray (Fog) Apparatus |
| ASTM B 368 : 2021 | Standard Test Method for Copper-Accelerated Acetic Acid-Salt Spray (Fog) Testing (CASS Test) |
| ASTM B 136 : 2023 | Standard Test Method for Measurement of Stain Resistance of Anodic Coatings on Aluminum |
| ASTM E 429 : 1978 : R1991 : EDT 1 | Test Method for Measurement and Calculation of Reflecting Characteristics of Metallic Surfaces Using Integrating Sphere Instruments (Withdrawn 1996) |
| ASTM B 137 : 1995 : R2014 | Standard Test Method for Measurement of Coating Mass Per Unit Area on Anodically Coated Aluminum |
| ASTM B 110 : 1945 : R1973 | Method of Dielectric Strength of Anodically Coated Aluminum (Withdrawn 1981) |
| ASTM D 658 : 1991 | Standard Test Method for Abrasion Resistance of Organic Coatings by Air Blast Abrasive (Withdrawn 1996) |
| ASTM B 244 : 2009 : R2021 | Standard Test Method for Measurement of Thickness of Anodic Coatings on Aluminum and of Other Nonconductive Coatings on Nonmagnetic Basis Metals with Eddy-Current Instruments |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.