ASTM B 650 : 2023
Current
The latest, up-to-date edition.
Standard Specification for Electrodeposited Engineering Chromium Coatings on Ferrous Substrates
English
15-12-2023
| Committee |
B 08
|
| DocumentType |
Standard
|
| Pages |
5
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Current
|
| Supersedes |
1.1This specification covers the requirements for electrodeposited chromium coatings applied to ferrous alloys for engineering applications.
1.2Electrodeposited engineering chromium, which is sometimes called “functional” or “hard” chromium, is usually applied directly to the basis metal and is much thicker than decorative chromium. Engineering chromium is used for the following:
1.2.1To increase wear and abrasion resistance,
1.2.2To increase fretting resistance,
1.2.3To reduce static and kinetic friction,
1.2.4To reduce galling or seizing, or both, for various metal combinations,
1.2.5To increase corrosion resistance, and
1.2.6To build up undersize or worn parts.
1.3This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.4This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
| ASTM F 1007 : 2018 : R2022 | Standard Specification for Pipeline Expansion Joints of the Packed Slip Type for Marine Application |
| ASTM B 765 : 2003 : R2023 | Standard Guide for Selection of Porosity and Gross Defect Tests for Electrodeposits and Related Metallic Coatings |
| ASTM B 177/B177M : 2011 : R2021 | Standard Guide for Engineering Chromium Electroplating |
| ASTM B 851 : 2004 : R2020 | Standard Specification for Automated Controlled Shot Peening of Metallic Articles Prior to Nickel, Autocatalytic Nickel, or Chromium Plating, or as Final Finish |
| ASTM B 117 : 2025 | Standard Practice for Operating Salt Spray (Fog) Apparatus |
| ASTM F 1459 : 2006 : R2017 | Standard Test Method for Determination of the Susceptibility of Metallic Materials to Hydrogen Gas Embrittlement (HGE) |
| ASTM B 487 : 2024 | Standard Test Method for Measurement of Metal and Oxide Coating Thickness by Microscopical Examination of Cross Section |
| ASTM F 1459 : 2006 : R2024 | Standard Test Method for Determination of the Susceptibility of Metallic Materials to Hydrogen Gas Embrittlement (HGE) |
| ASTM E 8 : 1999 | Standard Test Methods for Tension Testing of Metallic Materials |
| ASTM B 374 : 2024 | Standard Terminology Relating to Electroplating |
| ASTM B 487 : 2020 | Standard Test Method for Measurement of Metal and Oxide Coating Thickness by Microscopical Examination of Cross Section |
| ASTM B 242 : 1999 : R2025 | Standard Guide for Preparation of High-Carbon Steel for Electroplating |
| ASTM B 117 : 2019 | Standard Practice for Operating Salt Spray (Fog) Apparatus |
| ASTM B 320 : 2025 | Standard Practice for Preparation of Iron Castings for Electroplating |
| ASTM E 8 : 1991 | Standard Test Method of Tension Testing of Metallic Materials |
| ASTM B 374 : 2021 | Standard Terminology Relating to Electroplating |
| ASTM B 320 : 1960 : R2019 | Standard Practice for Preparation of Iron Castings for Electroplating |
| ASTM B 242 : 1999 : R2020 | Standard Guide for Preparation of High-Carbon Steel for Electroplating |
Access your standards online with a subscription
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.
Important note : Users cannot be edited or removed once added to your Multi user PDF.