ASTM B 756 : 2000 : R2011
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Specification for Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06110) Rod and Bar
Hardcopy , PDF
11-11-2014
English
01-10-2011
Important note : Users cannot be edited or removed once added to your Multi user PDF.CONTAINED IN VOL. 02.04, 2016 Defines nickel-chromiummolybdenum-tungsten (UNS N06110)2 in the form of hotworked rod and bar and cold-worked rod in the conditions.
| Committee |
B 02
|
| DocumentType |
Standard
|
| Pages |
5
|
| ProductNote |
Reconfirmed 2011
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Superseded
|
| SupersededBy |
1.1 This specification covers nickel-chromium-molybdenum-tungsten (UNS N06110) in the form of hot-worked rod and bar and cold-worked rod in the conditions shown in Table 1.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.
TABLE 1 Mechanical Properties
| Condition and Diameter or Distance Between Parallel Surfaces in. (mm) | Tensile Strength min, ksi (MPa) | Yield Strength (0.2% Offset), min, ksi (MPa) | Elongation in 2 in. or 50 mm or 4D, min, % |
|---|---|---|---|
| Cold-worked rods and hot-worked rod and bar, annealed: | |||
| Up to 4 (102), incl | 95 (655) | 45 (310) | 60 |
| Over 4 (102) to 10 (254), incl | 90 (621) | 40 (276) | 50 |
| Forging quality (all sizes) | A | A | A |
A Forging quality is furnished to chemical requirements and surface inspection only. No tensile properties are required.
| ASTM E 1473 : 2016 : REDLINE | Standard Test Methods for Chemical Analysis of Nickel, Cobalt and High-Temperature Alloys |
| ASTM E 527 : 2016 : REDLINE | Standard Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS) |
| ASTM E 8 : 2004 | Standard Test Methods for Tension Testing of Metallic Materials |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.