ASTM B 863 : 2023
Current
The latest, up-to-date edition.
Standard Specification for Titanium and Titanium Alloy Wire
Hardcopy , PDF
English
28-11-2023
Important note : Users cannot be edited or removed once added to your Multi user PDF.| Committee |
B 10
|
| DocumentType |
Standard
|
| Pages |
7
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Current
|
| Supersedes |
1.1This specification covers titanium and titanium alloy wire as follows:
1.1.1Grade 1—UNS R50250. Unalloyed titanium,
1.1.2Grade 2—UNS R50400. Unalloyed titanium,
1.1.2.1Grade 2H—UNS R50400. Unalloyed titanium (Grade 2 with 58 ksi (400 MPa) minimum UTS),
1.1.3Grade 3—UNS R50550. Unalloyed titanium,
1.1.4Grade 4—UNS R50700. Unalloyed titanium,
1.1.5Grade 5—UNS R56400. Titanium alloy (6 % aluminum, 4 % vanadium),
1.1.6Grade 6—UNS R54520. Titanium alloy (5 % aluminum, 2.5 % tin),
1.1.7Grade 7—UNS R52400. Unalloyed titanium plus 0.12 % to 0.25 % palladium,
1.1.7.1Grade 7H—UNS R52400. Unalloyed titanium plus 0.12 % to 0.25 % palladium (Grade 7 with 58 ksi (400 MPa) minimum UTS),
1.1.8Grade 9—UNS R56320. Titanium alloy (3 % aluminum, 2.5 % vanadium),
1.1.9Grade 11—UNS R52250. Unalloyed titanium plus 0.12 % to 0.25 % palladium,
1.1.10Grade 12—UNS R53400. Titanium alloy (0.3 % molybdenum, 0.8 % nickel),
1.1.11Grade 13—UNS R53413. Titanium alloy (0.5 % nickel, 0.05 % ruthenium),
1.1.12Grade 14—UNS R53414. Titanium alloy (0.5 % nickel, 0.05 % ruthenium),
1.1.13Grade 15—UNS R53415. Titanium alloy (0.5 % nickel, 0.05 % ruthenium),
1.1.14Grade 16—UNS R52402. Unalloyed titanium plus 0.04 % to 0.08 % palladium,
1.1.14.1Grade 16H—UNS R52402. Unalloyed titanium plus 0.04 % to 0.08 % palladium (Grade 16 with 58 ksi (400 MPa) minimum UTS),
1.1.15Grade 17—UNS R52252. Unalloyed titanium plus 0.04 % to 0.08 % palladium,
1.1.16Grade 18—UNS R56322. Titanium alloy (3 % aluminum, 2.5 % vanadium) plus 0.04 % to 0.08 % palladium,
1.1.17Grade 19—UNS R58640. Titanium alloy (3 % aluminum, 8 % vanadium, 6 % chromium, 4 % zirconium, 4 % molybdenum),
1.1.18Grade 20—UNS R58645. Titanium alloy (3 % aluminum, 8 % vanadium, 6 % chromium, 4 % zirconium, 4 % molybdenum) plus 0.04 % to 0.08 % palladium,
1.1.19Grade 21—UNS R58210. Titanium alloy (15 % molybdenum, 3 % aluminum, 2.7 % niobium, 0.25 % silicon),
1.1.20Grade 23—UNS R56407. Titanium alloy (6 % aluminum, 4 % vanadium with extra low interstitial elements, ELI),
1.1.21Grade 24—UNS R56405. Titanium alloy (6 % aluminum, 4 % vanadium) plus 0.04 % to 0.08 % palladium,
1.1.22Grade 25—UNS R56403. Titanium alloy (6 % aluminum, 4 % vanadium) plus 0.3 % to 0.8 % nickel and 0.04 % to 0.08 % palladium,
1.1.23Grade 26—UNS R52404. Unalloyed titanium plus 0.08 % to 0.14 % ruthenium,
1.1.23.1Grade 26H—UNS R52404. Unalloyed titanium plus 0.08 % to 0.14 % ruthenium (Grade 26 with 58 ksi (400 MPa) minimum UTS),
1.1.24Grade 27—UNS R52254. Unalloyed titanium plus 0.08 % to 0.14 % ruthenium,
1.1.25Grade 28—UNS R56323. Titanium alloy (3 % aluminum, 2.5 % vanadium) plus 0.08 % to 0.14 % ruthenium,
1.1.26Grade 29—UNS R56404. Titanium alloy (6 % aluminum, 4 % vanadium with extra low interstitial elements, ELI) plus 0.08 % to 0.14 % ruthenium,
1.1.27Grade 32—UNS R55111. Titanium alloy (5 % aluminum, 1 % tin, 1 % vanadium, 1 % zirconium, 0.8 % molybdenum),
1.1.28Grade 33—UNS R53442. Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),
1.1.29Grade 34—UNS R53445. Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),
1.1.30Grade 35—UNS R56340. Titanium alloy (4.5 % aluminum, 2 % molybdenum, 1.6 % vanadium, 0.5 % iron, 0.3 % silicon),
1.1.31Grade 36—UNS R58450. Titanium alloy (45 % niobium),
1.1.32Grade 37—UNS R52815. Titanium alloy (1.5 % aluminum),
1.1.33Grade 38—UNS R54250. Titanium alloy (4 % aluminum, 2.5 % vanadium, 1.5 % iron), and
1.1.34Grade 39—UNS R53390. Titanium alloy (0.25 % iron, 0.4 % silicon).
Note 1:H grade material is identical to the corresponding numeric grade (that is, Grade 2H = Grade 2) except for the higher guaranteed minimum UTS, and may always be certified as meeting the requirements of its corresponding numeric grade.
1.2The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.3This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
| ASTM F 1155 : 2010 : R2019 | Standard Practice for Selection and Application of Piping System Materials |
| ASTM E 1941 : 2010 : R2016 | Standard Test Method for Determination of Carbon in Refractory and Reactive Metals and Their Alloys by Combustion Analysis |
| ASTM E 1941 : 2010 : R2024 | Standard Test Method for Determination of Carbon in Refractory and Reactive Metals and Their Alloys by Combustion Analysis |
| ASTM E 8/E8M : 2024 | Standard Test Methods for Tension Testing of Metallic Materials |
| ASTM E 8/E8M : 2022 | Standard Test Methods for Tension Testing of Metallic Materials |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.