ASTM B 928 : 2004
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Specification for High Magnesium Aluminum-Alloy Sheet and Plate for Marine Service
Hardcopy , PDF
11-11-2014
English
01-02-2004
Important note : Users cannot be edited or removed once added to your Multi user PDF.CONTAINED IN VOL 02.02, 2004 Covers high magnesium marine application aluminum-alloy, in alloy-tempers, for flat sheet, coiled sheet, and plate.
| Committee |
B 07
|
| DocumentType |
Standard
|
| Pages |
10
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Superseded
|
| SupersededBy | |
| Supersedes |
1.1 This specification covers high magnesium (Note 1) marine application aluminum-alloy (Note 2), in those alloy-tempers shown in Table 2 [Table 3], for flat sheet, coiled sheet, and plate, in the mill finish:
Note 2The term high magnesium in the general sense includes those alloys containing 3 % or more nominal magnesium.
Note 1—Throughout this specification use of the term alloy in the general sense includes aluminum as well as aluminum alloy.
1.2 Alloy and temper designations are in accordance with ANSI H35.1 [H35.1M]. The equivalent Unified Numbering System alloy designations are those ofTable 1 preceded by A9, for example, A95083 for 5083 in accordance with Practice E 527.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore each system shall be used independently of each other. Combining values from the two systems may result in non-conformance with the standard.
1.4 For acceptance criteria for inclusion of new aluminum and aluminum alloys in this specification, see Annex A2.
| ASTM G 67 : 2013 | Standard Test Method for Determining the Susceptibility to Intergranular Corrosion of 5XXX Series Aluminum Alloys by Mass Loss After Exposure to Nitric Acid (NAMLT Test) |
| ASTM E 607 : 2002 | Standard Test Method for Atomic Emission Spectrometric Analysis Aluminum Alloys by the Point to Plane Technique Nitrogen Atmosphere |
| ASTM B 666/B666M : 2015 : REDLINE | Standard Practice for Identification Marking of Aluminum and Magnesium Products |
| ASTM B 557 : 2015 : REDLINE | Standard Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products |
| ASTM G 66 : 1999 | Standard Test Method for Visual Assessment of Exfoliation Corrosion Susceptibility of 5XXX Series Aluminum Alloys (ASSET Test) |
| ASTM E 716 : 2016 : REDLINE | Standard Practices for Sampling and Sample Preparation of Aluminum and Aluminum Alloys for Determination of Chemical Composition by Spark Atomic Emission Spectrometry |
| ASTM E 527 : 2016 : REDLINE | Standard Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS) |
| ASTM B 557M : 2015 : REDLINE | Standard Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products (Metric) |
| ASTM B 660 : 2015 : REDLINE | Standard Practices for Packaging/Packing of Aluminum and Magnesium Products |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.