ASTM C 1322 : 2015 : R2019
Current
The latest, up-to-date edition.
![header thumbnail](/images/publishers\astm_cover.gif)
Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics
Hardcopy , PDF
English
01-07-2019
The objective of this practice is to provide an efficient and consistent methodology to locate and characterize fracture origins in advanced ceramics.
Committee |
C 28
|
DocumentType |
Standard Practice
|
Pages |
50
|
ProductNote |
THIS STANDARD ALSO REFERS TO NIST Special Publication SP 960-16
|
PublisherName |
American Society for Testing and Materials
|
Status |
Current
|
Supersedes |
1.1The objective of this practice is to provide an efficient and consistent methodology to locate and characterize fracture origins in advanced ceramics. It is applicable to advanced ceramics that are brittle; that is, fracture that takes place with little or no preceding plastic deformation. In such materials, fracture commences from a single location which is termed the fracture origin. The fracture origin in brittle ceramics normally consists of some irregularity or singularity in the material which acts as a stress concentrator. In the parlance of the engineer or scientist, these irregularities are termed flaws or defects. The latter word should not be construed to mean that the material has been prepared improperly or is somehow faulty.
1.2Although this practice is primarily intended for laboratory test piece analysis, the general concepts and procedures may be applied to component fracture analyses as well. In many cases, component fracture analysis may be aided by cutting laboratory test pieces out of the component. Information gleaned from testing the laboratory pieces (for example, flaw types, general fracture features, fracture mirror constants) may then aid interpretation of component fractures. For more information on component fracture analysis, see Refs (1, 2).2
1.3This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.4This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM C 1273 : 2018 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Ambient Temperatures |
ASTM C 1576 : 2005 : R2017 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress Flexural Testing (Stress Rupture) at Ambient Temperature |
ASTM F 561 : 2019 | Standard Practice for Retrieval and Analysis of Medical Devices, and Associated Tissues and Fluids |
ASTM C 1361 : 2010 : R2019 | Standard Practice for Constant-Amplitude, Axial, Tension-Tension Cyclic Fatigue of Advanced Ceramics at Ambient Temperatures |
ASTM C 1465 : 2008 : R2019 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Flexural Testing at Elevated Temperatures |
ASTM C 1683 : 2010 : R2019 | Standard Practice for Size Scaling of Tensile Strengths Using Weibull Statistics for Advanced Ceramics |
ASTM C 1499 : 2019 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1366 : 2019 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Elevated Temperatures |
ASTM C 1557 : 2020 | Standard Test Method for Tensile Strength and Young's Modulus of Fibers |
ASTM C 1323 : 2016 | Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature |
ASTM C 1368 : 2018 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress Rate Strength Testing at Ambient Temperature |
ASTM C 1421 : 2018 | Standard Test Methods for Determination of Fracture Toughness of Advanced Ceramics at Ambient Temperature |
ASTM C 1495 : 2016 | Standard Test Method for Effect of Surface Grinding on Flexure Strength of Advanced Ceramics |
ASTM C 1684 : 2018 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature—Cylindrical Rod Strength |
ASTM D 7972 : 2014 | Standard Test Method for Flexural Strength of Manufactured Carbon and Graphite Articles Using Three-Point Loading at Room Temperature |
ASTM C 1834 : 2016 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress Flexural Testing (Stress Rupture) at Elevated Temperatures |
ASTM C 1862 : 2017 | Standard Test Method for the Nominal Joint Strength of End-Plug Joints in Advanced Ceramic Tubes at Ambient and Elevated Temperatures |
ASTM C 1036 : 2001 | Standard Specification for Flat Glass |
ASTM C 1499 : 2015 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1145 : 2019 | Standard Terminology of Advanced Ceramics |
ASTM C 1678 : 2010 : R2015 | Standard Practice for Fractographic Analysis of Fracture Mirror Sizes in Ceramics and Glasses |
ASTM C 1211 : 2018 | Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures |
ASTM C 1211 : 2013 | Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures |
ASTM C 1145 : 1998 | Standard Terminology of Advanced Ceramics |
ASTM C 1161 : 2002 : REV C : R2008 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1145 : 2006 | Standard Terminology of Advanced Ceramics |
ASTM F 109 : 2012 : R2018 | Standard Terminology Relating to Surface Imperfections on Ceramics |
ASTM C 1161 : 2002 : REV C : R2008 : EDT 1 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1036 : 2021 | Standard Specification for Flat Glass |
ASTM C 1499 : 2004 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1036 : 2006 | Standard Specification for Flat Glass |
ASTM C 1161 : 2018 : R2023 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1499 : 2003 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1499 : 2005 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1145 : 2005 | Standard Terminology of Advanced Ceramics |
ASTM C 1161 : 2002 : REV C : EDT 1 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1499 : 2009 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM F 109 : 2021 | Standard Terminology Relating to Surface Imperfections on Ceramics |
ASTM C 1678 : 2007 | Standard Practice for Fractographic Analysis of Fracture Mirror Sizes in Ceramics and Glasses |
ASTM C 1036 : 2016 | Standard Specification for Flat Glass |
ASTM C 1161 : 2002 : REV A | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1239 : 2006 : REV A | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM C 1145 : 2003 | Standard Terminology of Advanced Ceramics |
ASTM C 1678 : 2010 | Standard Practice for Fractographic Analysis of Fracture Mirror Sizes in Ceramics and Glasses |
ASTM C 1036 : 2011 | Standard Specification for Flat Glass |
ASTM C 1499 : 2008 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1239 : 2013 : R2018 | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM C 1161 : 2018 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1211 : 1998 : REV A | Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures |
ASTM C 1161 : 2002 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1499 : 2002 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 242 : 2020 : REV B | Standard Terminology of Ceramic Whitewares and Related Products |
ASTM C 1499 : 2001 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 242 : 2021 | Standard Terminology of Ceramic Whitewares and Related Products |
ASTM C 1239 : 2000 | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM C 162 : 2005 : R2015 | Standard Terminology of<brk type="line"/> Glass and Glass Products |
ASTM C 1145 : 2006 : R2013 | Standard Terminology of Advanced Ceramics |
ASTM C 1161 : 2013 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1678 : 2021 | Standard Practice for Fractographic Analysis of Fracture Mirror Sizes in Ceramics and Glasses |
ASTM C 1239 : 2000 : R2005 | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM C 1499 : 2009 : R2013 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1145 : 2002 | Standard Terminology of Advanced Ceramics |
ASTM C 1211 : 2018 : R2023 | Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures |
ASTM C 162 : 2023 | Standard Terminology of Glass and Glass Products |
ASTM C 1211 : 2002 | Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures |
ASTM C 1161 : 1994 : R1996 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1239 : 2006 | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM C 1145 : 2002 : REV A | Standard Terminology of Advanced Ceramics |
ASTM C 1036 : 2011 : EDT 1 | Standard Specification for Flat Glass |
ASTM C 1161 : 2002 : REV C | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1145 : 2001 | Standard Terminology of Advanced Ceramics |
ASTM C 1239 : 2013 | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM C 1239 : 2007 | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM C 1145 : 2006 : R2013 : EDT 1 | Standard Terminology of Advanced Ceramics |
ASTM C 1211 : 2002 : R2008 | Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures |
ASTM C 1036 : 1991 : R1997 | Standard Specification for Flat Glass |
ASTM C 1678 : 2009 | Standard Practice for Fractographic Analysis of Fracture Mirror Sizes in Ceramics and Glasses |
ASTM C 1161 : 2002 : REV B | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : Users cannot be edited or removed once added to your Multi user PDF.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.