ASTM C 1323 : 2016 : REDLINE
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature
28-04-2022
English
19-02-2016
Important note : Users cannot be edited or removed once added to your Multi user PDF.CONTAINED IN VOL. 15.01, 2017 Defines the determination of ultimate strength under monotonic loading of advanced ceramics in tubular form at ambient temperatures.
| Committee |
C 28
|
| DocumentType |
Redline
|
| Pages |
8
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Superseded
|
| SupersededBy |
1.1This test method covers the determination of ultimate strength under monotonic loading of advanced ceramics in tubular form at ambient temperatures. The ultimate strength as used in this test method refers to the strength obtained under monotonic compressive loading of C-ring specimens such as shown in Fig. 1 where monotonic refers to a continuous nonstop test rate with no reversals from test initiation to final fracture. This method permits a range of sizes and shapes since test specimens may be prepared from a variety of tubular structures. The method may be used with microminiature test specimens.
1.2The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.2.1Values expressed in this test method are in accordance with the International System of Units (SI) and IEEE/ASTM SI 10.
1.3This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
| BS ISO 18558:2015 | Fine ceramics (advanced ceramics, advanced technical ceramics). Test method for determining elastic modulus and bending strength of ceramic tube and rings |
| 17/30338431 DC : DRAFT SEP 2017 | BS ISO 19843 - ROLLING BEARINGS - CERAMIC BEARINGS BALLS - DETERMINATION OF THE STRENGTH BY NOTCHED BALL TEST |
| ASTM C 1683 : 2010 | Standard Practice for Size Scaling of Tensile Strengths Using Weibull Statistics for Advanced Ceramics |
| ASTM C 1683 : 2010 : R2015 | Standard Practice for Size Scaling of Tensile Strengths Using Weibull Statistics for Advanced Ceramics |
| ISO 18558:2015 | Fine ceramics (advanced ceramics, advanced technical ceramics) Test method for determining elastic modulus and bending strength of ceramic tube and rings |
| IEEE/ASTM SI_10-2010 | American National Standard for Metric Practice |
| ASTM C 1322 : 2015 : REDLINE | PRACTICE FOR FRACTOGRAPHY AND CHARACTERIZATION OF FRACTURE ORIGINS IN ADVANCED CERAMICS |
| ASTM E 337 : 2015 : REDLINE | Standard Test Method for Measuring Humidity with a Psychrometer (the Measurement of Wet- and Dry-Bulb Temperatures) |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.