ASTM C 1576 : 2005 : R2017
Current
The latest, up-to-date edition.
![header thumbnail](/images/publishers\astm_cover.gif)
Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress Flexural Testing (Stress Rupture) at Ambient Temperature
Hardcopy , PDF
English
01-02-2017
CONTAINED IN VOL. 15.01, 2017 Defines the determination of slow crack growth (SCG) parameters of advanced ceramics by using constant stress flexural testing in which time to failure of flexure test specimens is determined in four-point flexure as a function of constant applied stress in a given environment at ambient temperature.
Committee |
C 28
|
DocumentType |
Test Method
|
Pages |
13
|
ProductNote |
Reconfirmed 2017
|
PublisherName |
American Society for Testing and Materials
|
Status |
Current
|
Supersedes |
1.1This standard test method covers the determination of slow crack growth (SCG) parameters of advanced ceramics by using constant stress flexural testing in which time to failure of flexure test specimens is determined in four-point flexure as a function of constant applied stress in a given environment at ambient temperature. In addition, test specimen fabrication methods, test stress levels, data collection and analysis, and reporting procedures are addressed. The decrease in time to failure with increasing applied stress in a specified environment is the basis of this test method that enables the evaluation of slow crack growth parameters of a material. The preferred analysis in the present method is based on a power law relationship between crack velocity and applied stress intensity; alternative analysis approaches are also discussed for situations where the power law relationship is not applicable.
Note 1:The test method in this standard is frequently referred to as “static fatigue” or stress-rupture testing (1-3)2 in which the term “fatigue” is used interchangeably with the term “slow crack growth.” To avoid possible confusion with the “fatigue” phenomenon of a material that occurs exclusively under cyclic loading, as defined in Terminology E1823, this test method uses the term “constant stress testing” rather than “static fatigue” testing.
1.2This test method applies primarily to monolithic advanced ceramics that are macroscopically homogeneous and isotropic. This test method may also be applied to certain whisker- or particle-reinforced ceramics as well as certain discontinuous fiber-reinforced composite ceramics that exhibit macroscopically homogeneous behavior. Generally, continuous fiber ceramic composites do not exhibit macroscopically isotropic, homogeneous, continuous behavior, and the application of this test method to these materials is not recommended.
1.3This test method is intended for use with various test environments such as air, other gaseous environments, and liquids.
1.4The values stated in SI units are to be regarded as the standard and in accordance with IEEE/ASTM SI 10 Standard.
1.5This test method may involve hazardous materials, operations, and equipment. This standard does not purport to address all of the safety concerns associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
ASTM C 1674 : 2016 | Standard Test Method for Flexural Strength of Advanced Ceramics with Engineered Porosity (Honeycomb Cellular Channels) at Ambient Temperatures |
ASTM C 1834 : 2016 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress Flexural Testing (Stress Rupture) at Elevated Temperatures |
ASTM C 1145 : 2019 | Standard Terminology of Advanced Ceramics |
ASTM E 1823 : 2024 | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1368 : 2000 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Flexural Testing at Ambient Temperature |
ASTM C 1322 : 2005 : REV B | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM E 1823 : 2024 : REV A | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1145 : 1998 | Standard Terminology of Advanced Ceramics |
ASTM E 1823 : 2012 : REV : EDT 0 | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1161 : 2002 : REV C : R2008 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM E 1823 : 2007 : REV A | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1145 : 2006 | Standard Terminology of Advanced Ceramics |
ASTM C 1161 : 2002 : REV C : R2008 : EDT 1 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM E 1823 : 2009 : REV A | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1161 : 2018 : R2023 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1322 : 2015 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM C 1322 : 2005 : REV A | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM E 337 : 2015 : R2023 | Standard Test Method for Measuring Humidity with a Psychrometer (the Measurement of Wet- and Dry-Bulb Temperatures) |
ASTM C 1145 : 2005 | Standard Terminology of Advanced Ceramics |
ASTM C 1161 : 2002 : REV C : EDT 1 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM E 337 : 2015 | Standard Test Method for Measuring Humidity with a Psychrometer (the Measurement of Wet- and Dry-Bulb Temperatures) |
ASTM E 6 : 2002 | Standard Terminology Relating to Methods of Mechanical Testing |
ASTM C 1465 : 2008 : R2019 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Flexural Testing at Elevated Temperatures |
ASTM E 399 : 2020 : REV A | Standard Test Method for Linear-Elastic Plane-Strain Fracture Toughness of Metallic Materials |
ASTM C 1322 : 2005 : REV B : EDT 1 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM C 1161 : 2002 : REV A | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1368 : 2018 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress Rate Strength Testing at Ambient Temperature |
ASTM C 1145 : 2003 | Standard Terminology of Advanced Ceramics |
ASTM E 399 : 2023 | Standard Test Method for Linear-Elastic Plane-Strain Fracture Toughness of Metallic Materials |
ASTM E 1823 : 2005 : REV A : EDT 1 | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1368 : 2006 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Flexural Testing at Ambient Temperature |
ASTM E 1823 : 2010 : REV A | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM E 1823 : 2021 | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1322 : 2005 : REV B : R2010 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM C 1322 : 1996 : REV A | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM E 1823 : 2009 : REV B | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1161 : 2018 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1322 : 2015 : REDLINE | PRACTICE FOR FRACTOGRAPHY AND CHARACTERIZATION OF FRACTURE ORIGINS IN ADVANCED CERAMICS |
ASTM E 1823 : 2012 : REV D | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM E 1823 : 2012 : REV B | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1161 : 2002 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1322 : 2002 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM E 6 : 2015 : EDT 3 | Standard Terminology Relating to Methods of Mechanical Testing |
ASTM C 1465 : 2008 : R2013 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Flexural Testing at Elevated Temperatures |
ASTM C 1465 : 2000 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Flexural Testing at Elevated Temperatures |
ASTM C 1368 : 2001 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Flexural Testing at Ambient Temperature |
ASTM E 6 : 2023 : REV A | Standard Terminology Relating to Methods of Mechanical Testing |
ASTM C 1145 : 2006 : R2013 | Standard Terminology of Advanced Ceramics |
ASTM E 337 : 2015 : REDLINE | Standard Test Method for Measuring Humidity with a Psychrometer (the Measurement of Wet- and Dry-Bulb Temperatures) |
ASTM C 1161 : 2013 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1322 : 2002 : REV A | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM E 4 : 2021 | Standard Practices for Force Calibration and Verification of Testing Machines |
ASTM E 1823 : 1996 : R2002 | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1368 : 2010 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Strength Testing at Ambient Temperature |
ASTM E 1823 : 1996 : EDT 1 | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1145 : 2002 | Standard Terminology of Advanced Ceramics |
ASTM E 1823 : 2012 : REV A | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM E 1823 : 2007 | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1465 : 2000 : R2006 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Flexural Testing at Elevated Temperatures |
ASTM C 1322 : 2015 : R2019 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM E 6 : 2015 : EDT 4 : REDLINE | Standard Terminology Relating to Methods of Mechanical Testing |
ASTM C 1161 : 1994 : R1996 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1145 : 2002 : REV A | Standard Terminology of Advanced Ceramics |
ASTM C 1465 : 2008 : R2013 : EDT 1 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Flexural Testing at Elevated Temperatures |
ASTM C 1161 : 2002 : REV C | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1465 : 2008 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Flexural Testing at Elevated Temperatures |
ASTM E 112 : 2013 : R2021 | Standard Test Methods for Determining Average Grain Size |
ASTM E 112 : 2013 | Standard Test Methods for Determining Average Grain Size |
ASTM C 1322 : 2005 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM C 1368 : 2010 : R2017 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Strength Testing at Ambient Temperature |
ASTM E 1823 : 2023 | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM E 6 : 2015 : EDT 4 | Standard Terminology Relating to Methods of Mechanical Testing |
ASTM E 399 : 2022 | Standard Test Method for Linear-Elastic Plane-Strain Fracture Toughness of Metallic Materials |
ASTM E 6 : 2023 | Standard Terminology Relating to Methods of Mechanical Testing |
ASTM C 1145 : 2001 | Standard Terminology of Advanced Ceramics |
ASTM E 1823 : 2013 | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1145 : 2006 : R2013 : EDT 1 | Standard Terminology of Advanced Ceramics |
ASTM E 1823 : 2012 : REV C | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM E 1823 : 2020 : REV B | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM E 112 : 2024 | Standard Test Methods for Determining Average Grain Size |
ASTM E 1823 : 2005 : REV A | Standard Terminology Relating to Fatigue and Fracture Testing |
ASTM C 1161 : 2002 : REV B | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM E 1823 : 2011 | Standard Terminology Relating to Fatigue and Fracture Testing |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : Users cannot be edited or removed once added to your Multi user PDF.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.