Standard Test Methods for Sampling and Testing Coal Ash or Natural Pozzolans for Use in Concrete
Hardcopy , PDF
English
27-02-2024
Important note : Users cannot be edited or removed once added to your Multi user PDF.| Committee |
C 09
|
| DocumentType |
Test Method
|
| Pages |
11
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Current
|
| Supersedes |
1.1These test methods cover procedures for sampling and testing coal ash and raw or calcined pozzolans for use in concrete.
1.2The procedures appear in the following order:
| Sections | |
| Sampling | 7 |
| CHEMICAL ANALYSIS | |
| Reagents and apparatus | 10 |
| Moisture content | 11 and 12 |
| Loss on ignition | 13 and 14 |
| Silicon dioxide, aluminum oxide, iron oxide, | 15 |
| Available alkali | 16 and 17 |
| Ammonia | 18 |
| PHYSICAL TESTS | |
| Density | 19 |
| Fineness | 20 |
| Increase of drying shrinkage of mortar bars | 21 – 23 |
| Soundness | 24 |
| Air-entrainment of mortar | 25 and 26 |
| Strength activity index | 27 – 30 |
| Water requirement | 31 |
| Effectiveness of Coal Ash or Natural Pozzolan in | 32 |
| Effectiveness of Coal Ash or Natural Pozzolan in | 34 |
1.3The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.
Note 1:Sieve size is identified by its standard designation in Specification E11. The alternative designation given in parentheses is for information only and does not represent a different standard sieve size.
1.4This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.5The text of this standard references notes and footnotes that provide explanatory information. These notes and footnotes (excluding those in tables) shall not be considered as requirements of this standard.
1.6This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
| ASTM C 1697 : 2021 | Standard Specification for Blended Supplementary Cementitious Materials |
| ASTM D 242/D242M : 2019 | Standard Specification for Mineral Filler for Asphalt Mixtures |
| ASTM C 595/C595M : 2023 | Standard Specification for Blended Hydraulic Cements |
| ASTM D 5759 : 2012 : R2020 | Standard Guide for Characterization of Coal Fly Ash and Clean Coal Combustion Fly Ash for Potential Uses |
| ASTM C 1797 : 2023 : REV A | Standard Specification for Ground Calcium Carbonate and Aggregate Mineral Fillers for use in Hydraulic Cement Concrete |
| ASTM C 618 : 2023 : EDT 1 | Standard Specification for Coal Ash and Raw or Calcined Natural Pozzolan for Use in Concrete |
| ASTM C 1240 : 2020 | Standard Specification for Silica Fume Used in Cementitious Mixtures |
| ASTM C 802 : 2014 : R2022 | Standard Practice for Conducting an Interlaboratory Test Program to Determine the Precision of Test Methods for Construction Materials |
| ASTM E 1266 : 2020 | Standard Practice for Processing Mixtures of Lime, Fly Ash, and Heavy Metal Wastes in Structural Fills and Other Construction Applications |
| ASTM C 1709 : 2022 | Standard Guide for Evaluation of Alternative Supplementary Cementitious Materials (ASCM) for Use in Concrete |
| ASTM C 1866/C1866M : 2022 | Standard Specification for Ground-Glass Pozzolan for Use in Concrete |
| ASTM C 1778 : 2023 | Standard Guide for Reducing the Risk of Deleterious Alkali-Aggregate Reaction in Concrete |
| ASTM E 3355 : 2023 | Standard Guide for Characterization of Coal Combustion Products (CCPs) in Storage Area(s) for Beneficial Use |
| ASTM C 150/C150M : 2024 | Standard Specification for Portland Cement |
| ASTM C 670 : 2024 | Standard Practice for Preparing Precision and Bias Statements for Test Methods for Construction Materials |
| ASTM E 11 : 2024 | Standard Specification for Woven Wire Test Sieve Cloth and Test Sieves |
| ASTM C 125 : 2024 | Standard Terminology Relating to Concrete and Concrete Aggregates |
| ASTM C 109/C109M : 2021 | Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50mm] Cube Specimens) |
| ASTM C 157/C157M : 2017 | Standard Test Method for Length Change of Hardened Hydraulic-Cement Mortar and Concrete |
| ASTM C 204 : 2024 | Standard Test Methods for Fineness of Hydraulic Cement by Air-Permeability Apparatus |
| ASTM C 430 : 2017 | Standard Test Method for Fineness of Hydraulic Cement by the 45-μm (No. 325) Sieve |
| ASTM C 219 : 2020 : REV A | Standard Terminology Relating to Hydraulic and Other Inorganic Cements |
| ASTM C 430 : 2024 | Standard Test Method for Fineness of Hydraulic Cement by the 45-μm (No. 325) Sieve |
| ASTM C 151/C151M : 2018 | Standard Test Method for Autoclave Expansion of Hydraulic Cement |
| ASTM C 151/C151M : 2023 | Standard Test Method for Autoclave Expansion of Hydraulic Cement |
| ASTM E 11 : 2022 | Standard Specification for Woven Wire Test Sieve Cloth and Test Sieves |
| ASTM C 109/C109M : 2023 | Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 50mm [2 in.] Cube Specimens) |
| ASTM C 204 : 2023 | Standard Test Methods for Fineness of Hydraulic Cement by Air-Permeability Apparatus |
| ASTM C 157/C157M : 2024 : EDT 1 | Standard Test Method for Length Change of Hardened Hydraulic-Cement Mortar and Concrete |
| ASTM C 114 : 2024 | Standard Test Methods for Chemical Analysis of Hydraulic Cement |
| ASTM C 670 : 2024 : REV A | Standard Practice for Preparing Precision and Bias Statements for Test Methods for Construction Materials |
| ASTM C 114 : 2023 | Standard Test Methods for Chemical Analysis of Hydraulic Cement |
| ASTM C 157/C157M : 2024 | Standard Test Method for Length Change of Hardened Hydraulic-Cement Mortar and Concrete |
| ASTM C 595/C595M : 2024 | Standard Specification for Blended Hydraulic Cements |
| ASTM C 125 : 2021 : REV A | Standard Terminology Relating to Concrete and Concrete Aggregates |
| ASTM C 1012/C1012M : 2024 | Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution |
| ASTM C 1012/C1012M : 2024 : REV A | Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution |
| ASTM C 150/C150M : 2022 | Standard Specification for Portland Cement |
| ASTM C 1012/C1012M : 2018 : REV B | Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution |
| ASTM C 670 : 2015 | Standard Practice for Preparing Precision and Bias Statements for Test Methods for Construction Materials |
| ASTM C 1697 : 2024 | Standard Specification for Blended Supplementary Cementitious Materials |
| ASTM C 219 : 2024 | Standard Terminology Relating to Hydraulic and Other Inorganic Cements |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.