ASTM C 338 : 1993
Superseded
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
TEST METHOD FOR SOFTENING POINT OF GLASS
Superseded date
25-06-2017
Published date
01-01-2013
CONTAINED IN VOL. 15.02, 2017 Defines the determination of the softening point of a glass by determining the temperature at which a round fiber of the glass, nominally 0.65 mm in diameter and 235 mm long with specified tolerances, elongates under its own weight at a rate of 1 mm/min. when the upper 100 mm of its length is heated in a specified furnace at the rate of 5 +/-1 degrees C/min.
| Committee |
C 14
|
| DevelopmentNote |
Supersedes FED STD 626 (02/2004)
|
| DocumentType |
Standard
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Superseded
|
| Supersedes |
| Standards | Relationship |
| UNE 43701:1974 | Identical |
| ASTM C 1351M : 1996 : R2007 | Standard Test Method for Measurement of Viscosity of Glass Between 10<sup>4</sup> Pa·s and 10<sup>8</sup> Pa·s by Viscous Compression of a Solid Right Cylinder [Metric] |
| ASTM C 1351M : 1996 : R2012 | Standard Test Method for Measurement of Viscosity of Glass Between 10<sup>4</sup> Pa·s and 10<sup>8</sup> Pa·s by Viscous Compression of a Solid Right Cylinder [Metric] |
| ASTM F 79 : 1969 : R2015 | Standard Specification for Type 101 Sealing Glass |
| MIL G 47034 : A NOTICE 1 | GLASS, FILTER, COLORED |
| ASTM E 438 : 1992 | SPECIFICATION FOR GLASSES IN LABORATORY APPARATUS |
| ASTM F 79 : 1969 : R2010 | Standard Specification for Type 101 Sealing Glass |
| ASTM E 438 : 1992 : R2018 | Standard Specification for Glasses in Laboratory Apparatus |
| ASTM C 162 : 2005 : R2010 | Standard Terminology of Glass and Glass Products |
| ASTM F 105 : 1972 : R2000 | Standard Specification for Type 58 Borosilicate Sealing Glass |
| ASTM E 438 : 1992 : R2006 | Standard Specification for Glasses in Laboratory Apparatus |
| ASTM C 1350M : 1996 : R2013 | Standard Test Method for Measurement of Viscosity of Glass Between Softening Point and Annealing Range (Approximately 10<sup>8</sup> Pa·s to Approximately 10<sup>13</sup> Pa·s) by Beam Bending (Metric) |
| ASTM E 438 : 1992 : R2011 | Standard Specification for Glasses in Laboratory Apparatus |
| ASTM C 1350M : 1996 : R2003 | Standard Test Method for Measurement of Viscosity of Glass Between Softening Point and Annealing Range (Approximately 10<sup>8</sup> Pa·s to Approximately 10 <sup>13</sup> Pa·s) by Beam Bending (Metric) |
| ASTM C 1350M : 1996 : R2008 | Standard Test Method for Measurement of Viscosity of Glass Between Softening Point and Annealing Range (Approximately 10<sup>8</sup> Pa·s to Approximately 10 <sup>13</sup> Pa·s) by Beam Bending (Metric) |
| ASTM E 438 : 1992 : R2001 : EDT 1 | Standard Specification for Glasses in Laboratory Apparatus |
| ASTM C 1350M : 1996 | Standard Test Method for Measurement of Viscosity of Glass Between Softening Point and Annealing Range (Approximately 10<sup>8</sup> Pa - s to Approximately 10<sup>13</sup> Pa - s) by Beam Bending (Metric) |
| ASTM F 105 : 1972 : R2010 | Standard Specification for Type 58 Borosilicate Sealing Glass |
| ASTM C 162 : 2005 : R2015 | Standard Terminology of<brk type="line"/> Glass and Glass Products |
| ASTM C 336 : 1971 : R2000 | Standard Test Method for Annealing Point and Strain Point of Glass by Fiber Elongation |
| ASTM F 105 : 1972 : R2005 | Standard Specification for Type 58 Borosilicate Sealing Glass |
| ASTM E 438 : 1992 : R1996 | Standard Specification for Glasses in Laboratory Apparatus |
| ASTM C 336 : 1971 : R2005 | Standard Test Method for Annealing Point and Strain Point of Glass by Fiber Elongation |
| ASTM C 336 : 1971 : R2015 | Standard Test Method for Annealing Point and Strain Point of Glass by Fiber Elongation |
| ASTM F 105 : 1972 : R1995 : EDT 1 | Standard Specification for Type 58 Borosilicate Sealing Glass |
| ASTM C 162 : 2005 | Standard Terminology of Glass and Glass Products |
| ASTM F 105 : 1972 : R2015 | Standard Specification for Type 58 Borosilicate Sealing Glass |
| ASTM C 336 : 1971 : R1995 : EDT 1 | Standard Test Method for Annealing Point and Strain Point of Glass by Fiber Elongation |
| ASTM C 336 : 1971 : R2010 | Standard Test Method for Annealing Point and Strain Point of Glass by Fiber Elongation |
| A-A-52407 Revision A:1998 | GLASS, FILTER, COLORED |
| ASTM C 135M : 1996 | Standard Test Method for Measurement of Viscosity of Glass Between 10<sup>4</sup> Pa-s and 10<sup>8</sup> Pa-s by Viscous Compression of a Solid Right Cylinder [Metric] |
| ASTM C 1351M : 1996 : R2017 | Standard Test Method for Measurement of Viscosity of Glass Between 10<sup>4</sup> Pa·s and 10<sup>8</sup> Pa·s by Viscous Compression of a Solid Right Cylinder [Metric] |
| ASTM F 79 : 1969 : R1995 : EDT 1 | Standard Specification for Type 101 Sealing Glass |
| ASTM F 79 : 1969 : R2005 | Standard Specification for Type 101 Sealing Glass |
| ASTM C 1351M : 1996 : R2002 | Standard Test Method for Measurement of Viscosity of Glass Between 10<sup>4</sup> Pa-s and 10<sup>8</sup> Pa-s by Viscous Compression of a Solid Right Cylinder [Metric] |
| ASTM F 79 : 1969 : R2000 | Standard Specification for Type 101 Sealing Glass |
| DIN 52312-1:1983-09 | TESTING OF GLASS - DETERMINATION OF VISCOSITY - PRINCIPLES |
Sorry this product is not available in your region.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.