![header thumbnail](/images/publishers\astm_cover.gif)
ASTM D 1623 : 2017 : REDLINE
Current
The latest, up-to-date edition.
![header thumbnail](/images/publishers\astm_cover.gif)
Standard Test Method for Tensile and Tensile Adhesion Properties of Rigid Cellular Plastics
English
21-06-2017
CONTAINED IN VOL. 08.01, 2017 Defines the determination of the tensile and tensile adhesion properties of rigid cellular materials in the form of test specimens of standard shape under defined conditions of temperature, humidity, and testing machine speed.
Committee |
D 20
|
DocumentType |
Redline
|
Pages |
7
|
PublisherName |
American Society for Testing and Materials
|
Status |
Current
|
1.1This test method covers the determination of the tensile and tensile adhesion properties of rigid cellular materials in the form of test specimens of standard shape under defined conditions of temperature, humidity, and testing machine speed.
1.2Tensile properties shall be measured using any of three types of specimens:
1.2.1Type Ashall be the preferred specimen in those cases where enough sample material exists to form the necessary specimen.
1.2.2Type Bshall be the preferred specimen when only smaller specimens are available, as in sandwich panels, etc.
1.2.3Type Cshall be the preferred specimen for the determination of tensile adhesive properties of a cellular plastic to a substrate as in a sandwich panel (top and bottom substrate) or the bonding strength of a cellular plastic to a single substrate.
1.3The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to inch-pound units that are provided for information only and are not considered standard.
Note 1:There is no known ISO equivalent to this test method.
1.4This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
MIL P 24249 : A | PLASTIC MATERIAL, CELLULAR POLYURETHANE, RIGID, VOID FILLER, POUR-IN-PLACE, LARGE SCALE AND INSTALLATION OF |
MIL F 83671 : A | FOAM-IN-PLACE PACKAGING MATERIALS, GENERAL SPECIFICATION FOR |
I.S. EN 16245-5:2013 | FIBRE-REINFORCED PLASTIC COMPOSITES - DECLARATION OF RAW MATERIAL CHARACTERISTICS - PART 5: SPECIFIC REQUIREMENTS FOR CORE MATERIALS |
UNI EN 16245-5 : 2013 | FIBRE-REINFORCED PLASTIC COMPOSITES - DECLARATION OF RAW MATERIAL CHARACTERISTICS - PART 5: SPECIFIC REQUIREMENTS FOR CORE MATERIALS |
ASTM E 1730 : 2015 : REDLINE | SPECIFICATION FOR RIGID FOAM FOR USE IN STRUCTURAL SANDWICH PANEL CORES |
ASTM C 1330 : 2002 : R2007 | Standard Specification for Cylindrical Sealant Backing for Use with Cold Liquid Applied Sealants |
ASTM C 1512 : 2010 : R2015 : EDT 1 | Standard Test Method for Characterizing the Effect of Exposure to Environmental Cycling on Thermal Performance of Insulation Products |
ASTM D 7425 : 2008 | Standard Specification for Spray Polyurethane Foam Used for Roofing Applications |
ICC 2009 INT. RESI.CODE & COMM.-I1 : 2009 | 2009 INTERNATIONAL RESIDENTIAL CODE & COMMENTARY - VOLUME 2: CHAPTERS 12 TO 44 |
MIL-P-46847 Revision B:1984 | PLASTIC MATERIAL, FOAMED POLYURETHANE FOR ENCAPSULATING ELECTRONIC COMPONENTS |
MIL-HDBK-304 Revision C:1997 | PACKAGE CUSHIONING DESIGN |
BS EN 16245-5:2013 | Fibre-reinforced plastic composites. Declaration of raw material characteristics Specific requirements for core materials |
BS ISO 12891-2:2014 | Retrieval and analysis of surgical implants Analysis of retrieved surgical implants |
ASTM D 2341 : 1981 | Specification for Rigid Urethane Foam (Withdrawn 1988) |
MIL-PRF-83671 Revision B:1997 | FOAM-IN-PLACE PACKAGING MATERIALS, GENERAL SPECIFICATION FOR |
ASTM C 1330 : 2002 | Standard Specification for Cylindrical Sealant Backing for Use with Cold Liquid Applied Sealants |
ASTM F 2150 : 2013 : REDLINE | Standard Guide for Characterization and Testing of Biomaterial Scaffolds Used in Tissue-Engineered Medical Products |
ASTM C 1330 : 2002 : R2013 | Standard Specification for Cylindrical Sealant Backing for Use with Cold Liquid-Applied Sealants |
ASTM D 5249 : 2010 : R2016 | Standard Specification for Backer Material for Use with Cold- and Hot-Applied Joint Sealants in Portland-Cement Concrete and Asphalt Joints |
ASTM F 561 : 2013 | Standard Practice for Retrieval and Analysis of Medical Devices, and Associated Tissues and Fluids |
NASA MSFC PROC 3687 : 2015 | MATERIAL SPECIFICATION FOR POLYURETHANE FOAM - SPRAYABLE |
ASTM D 7425/D7425M : 2013 : REDLINE | Standard Specification for Spray Polyurethane Foam Used for Roofing Applications |
NASA MSFC SPEC 2083 : 2007 | MULTIPROGRAM/PROJECT COMMON USE DOCUMENT FOAM, POLYURETHANE |
ASTM D 5249 : 2010 | Standard Specification for Backer Material for Use with Cold- and Hot-Applied Joint Sealants in Portland-Cement Concrete and Asphalt Joints |
NASA MSFC SPEC 1919 : E2015 | MSFC TECHNICAL STANDARD ABLATIVE COMPOUND, THERMAL, APPLICATION AND CURE OF |
ASTM D 8139 : 2017 | Standard Specification for Semi-Rigid, Closed-Cell Polypropylene Foam, Preformed Expansion Joint Fillers for Concrete Paving and Structural Construction |
ASTM F 755:1999 | Standard Specification for Selection of Porous Polyethylene for Use in Surgical Implants |
ICC IRC CODE AND COMMENTARY VOLUME 2 : 2015 | IRC® Code and Commentary, Volume 2 |
NASA KSC MTB 175-88 : 1994 | PROCEDURE FOR CASUAL EXPOSURE OF MATERIALS TO HYPERGOLIC FLUIDS |
ICC 2012 INTERNATIONAL RESI. CODE : 2012 | INTERNATIONAL RESIDENTIAL CODE FOR ONE- AND TWO-FAMILY DWELLINGS |
NASA MSFC SPEC 3686 : A2015 | MATERIAL SPECIFICATION FOR POLYURETHANE FOAM - SPRAYABLE |
NASA MSFC SPEC 1918 : 1992 | ABLATIVE COMPOUND, THERMAL |
DIN EN 16245-5:2013-08 | Fibre-reinforced plastic composites - Declaration of raw material characteristics - Part 5: Specific requirements for core materials |
11/30239986 DC : DRAFT MAR 2011 | BS EN 16245-5 - FIBRE-REINFORCED PLASTIC COMPOSITES - DECLARATION OF RAW MATERIAL CHARACTERISTICS - PART 5: SPECIFIC REQUIREMENTS FOR CORE MATERIALS |
ASTM C 1512 : 2010 : R2015 | Standard Test Method for Characterizing the Effect of Exposure to Environmental Cycling on Thermal Performance of Insulation Products |
UNE-EN 16245-5:2014 | Fibre-reinforced plastic composites - Declaration of raw material characteristics - Part 5: Specific requirements for core materials |
13/30242622 DC : 0 | BS ISO 12891-2 - RETRIEVAL AND ANALYSIS OF SURGICAL IMPLANTS - PART 2: ANALYSIS OF RETRIEVED SURGICAL IMPLANTS |
ISO 12891-2:2014 | Retrieval and analysis of surgical implants Part 2: Analysis of retrieved surgical implants |
ASTM F 755 : 1999 : R2005 | Standard Specification for Selection of Porous Polyethylene for Use in Surgical Implants |
ASTM C 1029 : 2015 : REDLINE | Standard Specification for Spray-Applied Rigid Cellular Polyurethane Thermal Insulation |
ASTM C 1512 : 2010 | Standard Test Method for Characterizing the Effect of Exposure to Environmental Cycling on Thermal Performance of Insulation Products |
EN 16245-5:2013 | Fibre-reinforced plastic composites - Declaration of raw material characteristics - Part 5: Specific requirements for core materials |
MIL-P-47099 Revision A:1989 | POLYURETHANE FOAM, POLYETHER TYPE, RIGID, FOR PACKAGING AND ENCAPSULATION OF ELECTRONIC COMPONENTS |
ASTM F 755 : 1999 : EDT 1 | Standard Specification for Selection of Porous Polyethylene for Use in Surgical Implants |
ASTM E 1420 : 1991 | Practice for Specifying Polymeric Materials for Service in Ionizing Radiation Environments (Withdrawn 1996) |
ASTM F 755 : 1999 : R2011 | Standard Specification for Selection of Porous Polyethylene for Use in Surgical Implants |
ASTM D 638 : 2014 : REDLINE | Standard Test Method for Tensile Properties of Plastics |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : Users cannot be edited or removed once added to your Multi user PDF.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.