ASTM D 3039/D3039M : 2017 : REDLINE
Current
Current
The latest, up-to-date edition.
Standard Test Method for Tensile Properties of Polymer Matrix Composite Materials
Available format(s)
PDF
Language(s)
English
Published date
09-11-2017
Important note : Users cannot be edited or removed once added to your Multi user PDF.CONTAINED IN VOL. 15.03, 2017 Specifies the in-plane tensile properties of polymer matrix composite materials reinforced by high-modulus fibers.
| Committee |
D 30
|
| DevelopmentNote |
Supersedes ASTM D 3039. (01/2008)
|
| DocumentType |
Redline
|
| Pages |
16
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Current
|
1.1This test method determines the in-plane tensile properties of polymer matrix composite materials reinforced by high-modulus fibers. The composite material forms are limited to continuous fiber or discontinuous fiber-reinforced composites in which the laminate is balanced and symmetric with respect to the test direction.
1.2The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the inch-pound units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.
1.3This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.4This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
| AASHTO LRFDLTS 1 : 1900 | LRFD SPECIFICATIONS FOR STRUCTURAL SUPPORTS FOR HIGHWAY SIGNS, LUMINAIRES, AND TRAFFIC SIGNALS |
| 08/30168672 DC : DRAFT AUG 2008 | BS EN 15857 - NON-DESTRUCTIVE TESTING - ACOUSTIC EMISSION - TESTING OF FIBRE-REINFORCED POLYMERS - SPECIFIC METHODOLOGY AND GENERAL EVALUATION CRITERIA |
| ASTM D 8131/D8131M : 2017 | Standard Practice for Tensile Properties of Tapered and Stepped Joints of Polymer Matrix Composite Laminates |
| 04/30116297 DC : DRAFT JUL 2004 | ISO 20826 - ROAD VEHICLES - AUTOMOTIVE LPG COMPONENTS - CONTAINERS |
| ASTM F 1743 : 2017 : REDLINE | Standard Practice for Rehabilitation of Existing Pipelines and Conduits by Pulled-in-Place Installation of Cured-in-Place Thermosetting Resin Pipe (CIPP) |
| AASHTO MP 22 : 2013 : R2015 | SPECIFICATION FOR FIBER-REINFORCED POLYMER COMPOSITE MATERIALS FOR HIGHWAY AND BRIDGE STRUCTURES |
| ASTM D 5813 : 2004 | Standard Specification for Cured-In-Place Thermosetting Resin Sewer Piping Systems |
| IEC 61757-1-1:2016 | Fibre optic sensors - Part 1-1: Strain measurement - Strain sensors based on fibre Bragg gratings |
| ASTM E 1434 : 2000 | Standard Guide for Recording Mechanical Test Data of Fiber-Reinforced Composite Materials in Databases |
| ASTM E 1922 : 2004 | Standard Test Method for Translaminar Fracture Toughness of Laminated and Pultruded Polymer Matrix Composite Materials |
| ASTM E 1922 : 2004 : R2010 : EDT 1 | Standard Test Method for Translaminar Fracture Toughness of Laminated and Pultruded Polymer Matrix Composite Materials |
| ASTM D 6856/D6856M : 2003 : R2008 : EDT 1 | Standard Guide for Testing Fabric-Reinforced "Textile" Composite Materials |
| ASTM D 7616/D7616M : 2011 : R2017 | Standard Test Method for Determining Apparent Overlap Splice Shear Strength Properties of Wet Lay-Up Fiber-Reinforced Polymer Matrix Composites Used for Strengthening Civil Structures |
| CSA S808 : 2014 | SPECIFICATION FOR FIBRE-REINFORCED POLYMER (FRP) MATERIALS FOR EXTERNALLY REINFORCING STRUCTURES |
| 14/30273514 DC : 0 | BS ISO 18249 - NON-DESTRUCTIVE TESTING - ACOUSTIC EMISSION TESTING - TESTING OF FIBRE REINFORCED POLYMERS - SPECIFIC METHODOLOGY AND GENERAL EVALUATION CRITERIA |
| DIN EN 15857:2010-05 | Non-destructive testing - Acoustic emission - Testing of fibre-reinforced polymers - Specific methodology and general evaluation criteria |
| BS EN 61757-1-1:2017 | Fibre optic sensors Strain measurement. Strain sensors based on fibre Bragg gratings |
| UNI EN 15857 : 2010 | NON-DESTRUCTIVE TESTING - ACOUSTIC EMISSION - TESTING OF FIBRE-REINFORCED POLYMERS - SPECIFIC METHODOLOGY AND GENERAL EVALUATION CRITERIA |
| ASTM D 5083 : 2017 : REDLINE | Standard Test Method for Tensile Properties of Reinforced Thermosetting Plastics Using Straight-Sided Specimens |
| ASTM D 7745 : 2011 | Standard Practice for Testing Pultruded Composites |
| MIL-DTL-64154 Revision B:2008 | LAMINATE: FIBERGLASS-FABRIC-REINFORCED, PHENOLIC |
| ASTM D 7205/D7205M : 2006 : R2016 | Standard Test Method for Tensile Properties of Fiber Reinforced Polymer Matrix Composite Bars |
| ASTM F 2150 : 2013 : REDLINE | Standard Guide for Characterization and Testing of Biomaterial Scaffolds Used in Tissue-Engineered Medical Products |
| ASTM C 364/C364M : 2016 : REDLINE | Standard Test Method for Edgewise Compressive Strength of Sandwich Constructions |
| ASTM D 6856 : 2003 : R2008 | Standard Guide for Testing Fabric-Reinforced "Textile" Composite Materials |
| ASTM D 7205/D7205M : 2006 : R2011 | Standard Test Method for Tensile Properties of Fiber Reinforced Polymer Matrix Composite Bars |
| ASTM D 3518/D3518M : 2013-09 | TEST METHOD FOR IN-PLANE SHEAR RESPONSE OF POLYMER MATRIX COMPOSITE MATERIALS BY TENSILE TEST OF A +/-45 DEGREES LAMINATE |
| ASTM D 6856/D6856M : 2003 : R2016 | Standard Guide for Testing Fabric-Reinforced “Textile” Composite Materials |
| AASHTO MP 22 : 2013(R 2019) | SPECIFICATION FOR FIBER-REINFORCED POLYMER COMPOSITE MATERIALS FOR HIGHWAY AND BRIDGE STRUCTURES |
| ASTM D 7199 : 2007 | Standard Practice for Establishing Characteristic Values for Reinforced Glued Laminated Timber (Glulam) Beams Using Mechanics-Based Models |
| MIL-DTL-32265 Base Document:2007 | Folded Fiberglass Mat Fabrication and Packaging |
| MIL-PRF-46190 Revision A:1997 | PREPEGS, WOVEN FABRIC, CARBON FIBER, RESIN IMPREGNATED |
| ASTM E 1434 : 2000 : R2013 | Standard Guide for Recording Mechanical Test Data of Fiber-Reinforced Composite Materials in Databases (Withdrawn 2015) |
| ASTM D 5813 : 2004 : R2008 | Standard Specification for Cured-In-Place Thermosetting Resin Sewer Piping Systems |
| SAE AMS 2980/1 : 2014 | CARBON FIBER FABRIC AND EPOXY RESIN WET LAY-UP REPAIR MATERIAL - PART 1 - GENERAL REQUIREMENTS |
| SAE AMS 3970/1 : 2011 | CARBON FIBER FABRIC REPAIR PREPREG, 120 DEGREES C (250 DEGREES F) VACUUM CURING - PART 1 - GENERAL REQUIREMENTS |
| ASTM D 638 : 2014 : REDLINE | Standard Test Method for Tensile Properties of Plastics |
| ACI 440.2R : 2017 | GUIDE FOR THE DESIGN AND CONSTRUCTION OF EXTERNALLY BONDED FRP SYSTEMS FOR STRENGTHENING CONCRETE STRUCTURES |
| ACI 440.7R : 2010 | GUIDE FOR THE DESIGN AND CONSTRUCTION OF EXTERNALLY BONDED FIBER-REINFORCED POLYMER SYSTEMS FOR STRENGTHENING UNREINFORCED MASONRY STRUCTURES |
| ASTM E 1922 : 2004 : R2015 | Standard Test Method for Translaminar Fracture Toughness of Laminated and Pultruded Polymer Matrix Composite Materials |
| EN 61757-1-1:2017 | Fibre optic sensors – Part 1-1: Strain measurement – Strain sensors based on fibre Bragg gratings |
| CSA S806: 2012 | DESIGN AND CONSTRUCTION OF BUILDING STRUCTURES WITH FIBRE-REINFORCED POLYMERS |
| ASTM D 6484/D6484M : 2014 : REDLINE | Standard Test Method for Open-Hole Compressive Strength of Polymer Matrix Composite Laminates |
| ACI MNL 3 : 0 | GUIDE TO THE CODE FOR ASSESSMENT, REPAIR, AND REHABILITATION OF EXISTING CONCRETE STRUCTURES |
| ASTM D 7205/D7205M:2006 | Standard Test Method for Tensile Properties of Fiber Reinforced Polymer Matrix Composite Bars |
| BS EN 15857:2010 | Non-destructive testing. Acoustic emission. Testing of fibre-reinforced polymers. Specific methodology and general evaluation criteria |
| SAE AMS 3970/6 : 2011 | CARBON FIBER FABRIC REPAIR PREPREG, 120 DEGREES C (250 DEGREES F) VACUUM CURING - PART 6 - MATERIAL SPECIFICATION: CARBON FIBER FABRIC REINFORCED EPOXY PREPREG FOR REPAIR, PLAIN WEAVE FABRIC, 193 G/M[2], ADHESIVE FILM FOR REPAIR AND NON-STRUCTURAL GLASS FIBER FABRIC REINFORCED EPOXY PREPREG, 105 G/M[2] |
| ASTM D 7199 : 2007 : R2012 | Standard Practice for Establishing Characteristic Values for Reinforced Glued Laminated Timber (Glulam) Beams Using Mechanics-Based Models |
| ASTM D 7616/D7616M : 2011 | Standard Test Method for Determining Apparent Overlap Splice Shear Strength Properties of Wet Lay-Up Fiber-Reinforced Polymer Matrix Composites Used for Strengthening Civil Structures |
| BS ISO 18249:2015 | Non-destructive testing. Acoustic emission testing. Specific methodology and general evaluation criteria for testing of fibre-reinforced polymers |
| MIL-PRF-46187 Revision A:1998 | PREPREG, UNIDIRECTIONAL TAPE, CARBON (GRAPHITE) FIBER HIGH TEMPERATURE RESIN IMPREGNATED, 316 DEGREES C (600 DEGREES F) |
| ASTM F 2019 : 2011 : REDLINE | Standard Practice for Rehabilitation of Existing Pipelines and Conduits by the Pulled in Place Installation of Glass Reinforced Plastic (GRP) Cured-in-Place Thermosetting Resin Pipe (CIPP) |
| ASTM C 297/C297M : 2016 : REDLINE | Standard Test Method for Flatwise Tensile Strength of Sandwich Constructions |
| ASTM E 1434 : 2000 : R2006 | Standard Guide for Recording Mechanical Test Data of Fiber-Reinforced Composite Materials in Databases |
| ISO 18249:2015 | Non-destructive testing Acoustic emission testing Specific methodology and general evaluation criteria for testing of fibre-reinforced polymers |
| EN 15857:2010 | Non-destructive testing - Acoustic emission - Testing of fibre-reinforced polymers - Specific methodology and general evaluation criteria |
| ASTM D 7565/D7565M : 2010 | Standard Test Method for Determining Tensile Properties of Fiber Reinforced Polymer Matrix Composites Used for Strengthening of Civil Structures |
| ASTM C 1275 : 2018 : REDLINE | Standard Test Method for Monotonic Tensile Behavior of Continuous Fiber-Reinforced Advanced Ceramics with Solid Rectangular Cross-Section Test Specimens at Ambient Temperature |
| ASTM D 6856 : 2003 | Standard Guide for Testing Fabric-Reinforced "Textile" Composite Materials |
| ASTM D 7565/D7565M : 2010 : R2017 | Standard Test Method for Determining Tensile Properties of Fiber Reinforced Polymer Matrix Composites Used for Strengthening of Civil Structures |
| ASTM D 5813 : 2004 : R2012 | Standard Specification for Cured-In-Place Thermosetting Resin Sewer Piping Systems |
| I.S. EN 15857:2010 | NON-DESTRUCTIVE TESTING - ACOUSTIC EMISSION - TESTING OF FIBRE-REINFORCED POLYMERS - SPECIFIC METHODOLOGY AND GENERAL EVALUATION CRITERIA |
| ASTM E 122 : 2017 : REDLINE | Standard Practice for Calculating Sample Size to Estimate, With Specified Precision, the Average for a Characteristic of a Lot or Process |
| ASTM E 177 : 2014 : REDLINE | Standard Practice for Use of the Terms Precision and Bias in ASTM Test Methods |
| ASTM D 5229/D5229M : 2014-06 | TEST METHOD FOR MOISTURE ABSORPTION PROPERTIES AND EQUILIBRIUM CONDITIONING OF POLYMER MATRIX COMPOSITE MATERIALS |
| ASTM D 792 : 2013 : REDLINE | Standard Test Methods for Density and Specific Gravity (Relative Density) of Plastics by Displacement |
| ASTM E 83 : 2016 : REDLINE | Standard Practice for Verification and Classification of Extensometer Systems |
| ASTM E 132 : 2017 : REDLINE | Standard Test Method for Poisson’s Ratio at Room Temperature |
| ASTM D 2734 : 2016 : REDLINE | Standard Test Methods for Void Content of Reinforced Plastics |
| ASTM D 3171 : 2015 : REDLINE | Standard Test Methods for Constituent Content of Composite Materials |
| ASTM E 111 : 2017 : REDLINE | Standard Test Method for Young’s Modulus, Tangent Modulus, and Chord Modulus |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.