ASTM D 3380 : 1990 : R1995 : EDT 1
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Test Method for Relative Permittivity (Dielectric Constant) and Dissipation Factor of Polymer-Based Microwave Circuit Substrates
Hardcopy , PDF
11-11-2014
English
01-01-1995
Important note : Users cannot be edited or removed once added to your Multi user PDF.| Committee |
D 09
|
| DocumentType |
Test Method
|
| Pages |
12
|
| ProductNote |
Reconfirmed EDT 1
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Superseded
|
| SupersededBy |
1.1 This test method permits the rapid measurement of apparent relative permittivity and loss tangent (dissipation factor) of metal-clad polymer-based circuit substrates in the X-band (8 to 12.4 GHz).
1.2 This test method is suitable for testing PTFE (polytetrafluorethylene) impregnated glass cloth or random-oriented fiber mats, glass fiber-reinforced polystyrene, polyphenyleneoxide, irradiated polyethylene, and similar materials having a nominal specimen thickness of 1.6 mm. The materials are applicable to service at nominal frequency of 9.6 GHz.
Note 1-See Appendix X1. for additional information about range of permittivity, thickness other than 1.6 mm, and tests at frequencies other than 9.6 GHz.1.3 The values stated in inch-pound units are to be regarded as the standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.