ASTM E 1356 : 2008
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Test Method for Assignment of the Glass Transition Temperatures by Differential Scanning Calorimetry
Hardcopy , PDF
17-08-2023
English
01-09-2008
Important note : Users cannot be edited or removed once added to your Multi user PDF.CONTAINED IN VOL. 14.02, 2015 Defines the assignment of the glass transition temperatures of materials using differential scanning calorimetry or differential thermal analysis.
| Committee |
E 37
|
| DocumentType |
Test Method
|
| Pages |
4
|
| ProductNote |
Reconfirmed 2008
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Superseded
|
| SupersededBy | |
| Supersedes |
1.1 This test method covers the assignment of the glass transition temperatures of materials using differential scanning calorimetry or differential thermal analysis.
1.2 This test method is applicable to amorphous materials or to partially crystalline materials containing amorphous regions, that are stable and do not undergo decomposition or sublimation in the glass transition region.
1.3 The normal operating temperature range is from −120 to 500 °C. The temperature range may be extended, depending upon the instrumentation used.
1.4 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.5 ISO standards 11357–2 is equivalent to this standard.
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
| ASTM D 1676 : 2017 | Standard Test Methods for Film-Insulated Magnet Wire |
| ASTM D 7338 : 2014 | Standard Guide for Assessment Of Fungal Growth in Buildings |
| ASTM D 3794 : 2018 | Standard Guide for Testing Coil Coatings |
| ASTM F 2902 : 2016 : EDT 1 | Standard Guide for Assessment of Absorbable Polymeric Implants |
| ASTM F 2150 : 2013 | Standard Guide for Characterization and Testing of Biomaterial Scaffolds Used in Tissue-Engineered Medical Products |
| ASTM F 2313 : 2018 | Standard Specification for Poly(glycolide) and Poly(glycolide-co-lactide) Resins for Surgical Implants with Mole Fractions Greater Than or Equal to 70 % Glycolide |
| ASTM F 1925 : 2017 | Standard Specification for Semi-Crystalline Poly(lactide) Polymer and Copolymer Resins for Surgical Implants |
| ASTM E 2602 : 2009 : R2015 | Standard Test Methods for the Assignment of the Glass Transition Temperature by Modulated Temperature Differential Scanning Calorimetry |
| ASTM D 7957/D7957M : 2017 | Standard Specification for Solid Round Glass Fiber Reinforced Polymer Bars for Concrete Reinforcement |
| ASTM D 6604 : 2000 : R2017 | Standard Practice for Glass Transition Temperatures of Hydrocarbon Resins by Differential Scanning Calorimetry |
| ASTM E 177 : 2014 : REDLINE | Standard Practice for Use of the Terms Precision and Bias in ASTM Test Methods |
| ISO 11357-2:2013 | Plastics Differential scanning calorimetry (DSC) Part 2: Determination of glass transition temperature and glass transition step height |
| ASTM E 1142 : 2015 : REDLINE | Standard Terminology Relating to Thermophysical Properties |
| ASTM E 473 : 2016-05 | TERMINOLOGY RELATING TO THERMAL ANALYSIS AND RHEOLOGY |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.