ASTM E 1824 : 2013
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Test Method for Assignment of a Glass Transition Temperature Using Thermomechanical Analysis: Tension Method
Hardcopy , PDF
21-08-2018
English
01-08-2013
Important note : Users cannot be edited or removed once added to your Multi user PDF.| Committee |
E 37
|
| DocumentType |
Test Method
|
| Pages |
4
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Superseded
|
| SupersededBy | |
| Supersedes |
1.1This test method covers a procedure for the assignment of a glass transition temperature (Tg) of materials on heating using thermomechanical measurements in tension.
1.2This test method may be used as a complement to Test Method E1545 and is applicable to amorphous or to partially crystalline materials in the form of films, fibers, wires, etc., that are sufficiently rigid to inhibit extension during loading at ambient temperature.
1.3The generally applicable temperature range for this test method is −100 to 600°C. This temperature range may be altered depending upon the instrumentation used.
1.4The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.5There is no ISO method equivalent to this standard.
1.6This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.