ASTM E 2347 : 2016 : REDLINE
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Test Method for Indentation Softening Temperature by Thermomechanical Analysis
13-08-2021
English
01-04-2016
Important note : Users cannot be edited or removed once added to your Multi user PDF.CONTAINED IN VOL. 14.02, 2016 Pertains to materials that soften upon heating to a modulus less than 6.0 MPa.
| Committee |
E 37
|
| DocumentType |
Redline
|
| Pages |
7
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Superseded
|
| SupersededBy |
1.1This test method is applicable to materials that soften upon heating to a modulus less than 6.0 MPa. This test method describes the determination of the temperature at which the specific modulus of either 6.65 (Method A) or 33.3 MPa (Method B) (equivalent to Test Method D1525) of a test specimen is realized by indentation measurement using a thermomechanical analyzer as the test specimen is heated. This temperature is identified as the indentation softening temperature. The test may be performed over the temperature range of ambient to 300°C.
Note 1:This test method is intended to provide results similar to those of Test Method D1525 but is performed on a thermomechanical analyzer using a smaller diameter indenting probe. Equivalence of results to those obtained by Test Method D1525 has been demonstrated on a limited number of materials. Until the user demonstrates equivalence, the results of this Test Method shall be considered to be independent and unrelated to those of Test Method D1525.
1.2This test method is not recommended for ethyl cellulose, poly (vinyl chloride), poly (vinylidene chloride) and other materials having a large measurement imprecision (see Test Method D1525 and 5.3 and Section 14).
1.3The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.4There is no ISO standard equivalent to this test method.
1.5This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
| ASTM D 1525 : 2017 | Standard Test Method for Vicat Softening Temperature of Plastics |
| ASTM E 1142 : 2015 : REDLINE | Standard Terminology Relating to Thermophysical Properties |
| ASTM E 473 : 2016-05 | TERMINOLOGY RELATING TO THERMAL ANALYSIS AND RHEOLOGY |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.