ASTM E 399 : 2017

1.1This test method covers the determination of fracture toughness (K_Ic) of metallic materials under predominantly linear-elastic, plane-strain conditions using fatigue precracked specimens having a thickness of 1.6 mm (0.063 in.) or greater2 subjected to slowly, or in special (elective) cases rapidly, increasing crack-displacement force. Details of test apparatus, specimen configuration, and experimental procedure are given in the Annexes.

1.2This test method is divided into two parts. The first part gives general recommendations and requirements for K_Ic testing. The second part consists of Annexes that give specific information on displacement gage and loading fixture design, special requirements for individual specimen configurations, and detailed procedures for fatigue precracking. Additional annexes are provided that give specific procedures for beryllium and rapid-force testing.

1.3General information and requirements common to all specimen configurations:

1.4Specific requirements related to test apparatus:

1.5Specific requirements related to individual specimen configurations:

1.6Specific requirements related to special test procedures:

1.7The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.

1.8This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.9This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.