ASTM E 415 : 2021 : REDLINE
Current
The latest, up-to-date edition.
Standard Test Method for Analysis of Carbon and Low-Alloy Steel by Spark Atomic Emission Spectrometry
English
27-10-2021
Important note : Users cannot be edited or removed once added to your Multi user PDF.| Committee |
E 01
|
| DocumentType |
Redline
|
| Pages |
24
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Current
|
| Supersedes |
1.1This test method covers the simultaneous determination of 21 alloying and residual elements in carbon and low-alloy steels by spark atomic emission vacuum spectrometry in the mass fraction ranges shown Note 1.
| Element | Composition Range, % | |
| Applicable Range, | Quantitative Range, | |
| Aluminum | 0 to 0.093 | 0.006 to 0.093 |
| Antimony | 0 to 0.027 | 0.006 to 0.027 |
| Arsenic | 0 to 0.1 | 0.003 to 0.1 |
| Boron | 0 to 0.007 | 0.0004 to 0.007 |
| Calcium | 0 to 0.003 | 0.002 to 0.003 |
| Carbon | 0 to 1.1 | 0.02 to 1.1 |
| Chromium | 0 to 8.2 | 0.007 to 8.14 |
| Cobalt | 0 to 0.20 | 0.006 to 0.20 |
| Copper | 0 to 0.5 | 0.006 to 0.5 |
| LeadC | 0 to 0.2 | 0.002 to 0.2 |
| Manganese | 0 to 2.0 | 0.03 to 2.0 |
| Molybdenum | 0 to 1.3 | 0.007 to 1.3 |
| Nickel | 0 to 5.0 | 0.006 to 5.0 |
| Niobium | 0 to 0.12 | 0.003 to 0.12 |
| Nitrogen | 0 to 0.015 | 0.01 to 0.055 |
| Phosphorous | 0 to 0.085 | 0.006 to 0.085 |
| Silicon | 0 to 1.54 | 0.02 to 1.54 |
| Sulfur | 0 to 0.055 | 0.001 to 0.055 |
| Tin | 0 to 0.061 | 0.005 to 0.061 |
| Titanium | 0 to 0.2 | 0.001 to 0.2 |
| Vanadium | 0 to 0.3 | 0.003 to 0.3 |
| Zirconium | 0 to 0.05 | 0.01 to 0.05 |
Note 1:The mass fraction ranges of the elements listed have been established through cooperative testing2 of reference materials.
1.2This test method covers analysis of specimens having a diameter adequate to overlap and seal the bore of the spark stand opening. The specimen thickness can vary significantly according to the design of the spectrometer stand, but a thickness between 10 mm and 38 mm has been found to be most practical.
1.3This test method covers the routine control analysis in iron and steelmaking operations and the analysis of processed material. It is designed for chill-cast, rolled, and forged specimens. Better performance is expected when reference materials and specimens are of similar metallurgical condition and composition. However, it is not required for all applications of this standard.
1.4This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.5This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.