ASTM E 601 : 2015 : REDLINE
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Guide for Measuring Electromotive Force (emf) Stability of Base-Metal Thermoelement Materials with Time in Air
29-12-2020
English
01-05-2015
Important note : Users cannot be edited or removed once added to your Multi user PDF.CONTAINED IN VOL. 14.03, 2017 Gives a method for measuring the emf stability of base-metal thermoelement materials in air referenced to platinum at specified constant elevated temperatures using dual, simultaneous, emf indicators, or using a single emf indicator, with the test and reference emf measured alternately.
| Committee |
E 20
|
| DocumentType |
Redline
|
| Pages |
7
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Superseded
|
| SupersededBy |
1.1This guide provides a method for measuring the emf stability of base-metal thermoelement materials in air referenced to platinum at specified constant elevated temperatures using dual, simultaneous, emf indicators, or using a single emf indicator, with the test and reference emf measured alternately. This test is conducted over a period of weeks.
1.2A calibrated platinum-rhodium/platinum thermocouple is used as a reference standard to establish the test temperature.
1.3The useful life of a thermocouple depends on the stability of the emf generated at given temperatures for a required time interval. This method provides a quantitative measure of the stability of individual thermoelements. By combining the results of the positive (P) and negative (N) thermoelements, the stability of a thermocouple comprised of both P and N thermoelements may be obtained. The emf of an individual thermoelement is measured against platinum, which may be the platinum leg of the platinum-rhodium/platinum reference thermocouple, or an additional platinum reference.
Note 1:Some thermoelements may show insignificant emf drift while undergoing relatively rapid oxidation. In these cases, failure of the thermoelement may be indicated only by a large rise in the electrical resistance between joined thermoelements, as measured at the reference junctions.
Note 2:See ASTM MNL 12 for recommended upper temperature limits in air.2
Note 3:This guide is only applicable for initially new thermoelements. Base-metal thermoelements exposed to temperatures above 200°C become thermoelectrically inhomogeneous, and stability testing of inhomogeneous thermoelements will give ambiguous results.
1.4This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
| ASTM E 344 : 2016-12 | TERMINOLOGY RELATING TO THERMOMETRY AND HYDROMETRY |
| ASTM E 230 : 2003 | Standard Specification and Temperature-Electromotive Force (EMF) Tables for Standardized Thermocouples |
| ASTM E 344 : 2016-12 | TERMINOLOGY RELATING TO THERMOMETRY AND HYDROMETRY |
| ASTM E 220 : 2013 : REDLINE | Standard Test Method for Calibration of Thermocouples By Comparison Techniques |
| ASTM E 1159 : 2015 : REDLINE | Standard Specification for Thermocouple Materials, Platinum-Rhodium Alloys, and Platinum |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.