ASTM G 111 : 1997 : R2018
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Guide for Corrosion Tests in High Temperature or High Pressure Environment, or Both
Hardcopy , PDF
11-11-2021
English
07-11-2018
This guide covers procedures, specimens, and equipment for conducting laboratory corrosion tests on metallic materials under conditions of high pressure (HP) or the combination of high temperature and high pressure (HTHP). See 3.2 for definitions of high pressure and temperature.
Committee |
G 01
|
DocumentType |
Guide
|
Pages |
5
|
ProductNote |
Reconfirmed 1997
|
PublisherName |
American Society for Testing and Materials
|
Status |
Superseded
|
SupersededBy | |
Supersedes |
1.1This guide covers procedures, specimens, and equipment for conducting laboratory corrosion tests on metallic materials under conditions of high pressure (HP) or the combination of high temperature and high pressure (HTHP). See 3.2 for definitions of high pressure and temperature.
1.2Tests conducted under HP or HTHP by their nature have special requirements. This guide establishes the basic considerations that are necessary when these conditions must be incorporated into laboratory corrosion tests.
1.3The procedures and methods in this guide are applicable for conducting mass loss corrosion, localized corrosion, and electrochemical tests as well as for use in environmentally induced cracking tests that need to be conducted under HP or HTHP conditions.
1.4The primary purpose for this guide is to promote consistency of corrosion test results. Furthermore, this guide will aid in the comparison of corrosion data between laboratories or testing organizations that utilize different equipment.
1.5The values stated in SI units are to be regarded as standard. The values given in parentheses are for information only.
1.6This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.7This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM G 146 : 2001 : R2018 | Standard Practice for Evaluation of Disbonding of Bimetallic Stainless Alloy/Steel Plate for Use in High-Pressure, High-Temperature Refinery Hydrogen Service |
ASTM G 170 : 2006 : R2020 : EDT 1 | Standard Guide for Evaluating and Qualifying Oilfield and Refinery Corrosion Inhibitors in the Laboratory |
ASTM G 205 : 2016 | Standard Guide for Determining Emulsion Properties, Wetting Behavior, and Corrosion-Inhibitory Properties of Crude Oils |
ASTM G 208 : 2012 : R2020 | Standard Practice for Evaluating and Qualifying Oilfield and Refinery Corrosion Inhibitors Using Jet Impingement Apparatus |
ASTM G 142 : 1998 : R2016 | Standard Test Method for Determination of Susceptibility of Metals to Embrittlement in Hydrogen Containing Environments at High Pressure, High Temperature, or Both |
ASTM G 129 : 2021 | Standard Practice for Slow Strain Rate Testing to Evaluate the Susceptibility of Metallic Materials to Environmentally Assisted Cracking |
ASTM G 184 : 2006 : R2020 : EDT 1 | Standard Practice for Evaluating and Qualifying Oil Field and Refinery Corrosion Inhibitors Using Rotating Cage |
ASTM G 185 : 2006 : R2020 : EDT 1 | Standard Practice for Evaluating and Qualifying Oil Field and Refinery Corrosion Inhibitors Using the Rotating Cylinder Electrode |
ASTM E 8/E8M : 2016 : REV A : EDT 1 | Standard Test Methods for Tension Testing of Metallic Materials |
ASTM G 59 : 1997 | Standard Test Method for Conducting Potentiodynamic Polarization Resistance Measurements |
ASTM E 8/E8M : 2021 | Standard Test Methods for Tension Testing of Metallic Materials |
ASTM G 38 : 2001 : R2013 | Standard Practice for Making and Using C-Ring Stress-Corrosion Test Specimens |
ASTM G 78 : 2015 : REDLINE | Standard Guide for Crevice Corrosion Testing of Iron-Base and Nickel-Base Stainless Alloys in Seawater and Other Chloride-Containing Aqueous Environments |
ASTM G 5 : 1994 | Standard Reference Test Method for Making Potentiostatic and Potentiodynamic Anodic Polarization Measurements |
ASTM G 39 : 1999 : R2016 | Standard Practice for Preparation and Use of Bent-Beam Stress-Corrosion Test Specimens |
ASTM G 5 : 1994 : R1999 | Standard Reference Test Method for Making Potentiostatic and Potentiodynamic Anodic Polarization Measurements |
ASTM G 5 : 2014 : EDT 1 | Standard Reference Test Method for Making Potentiodynamic Anodic Polarization Measurements |
ASTM G 31 : 2021 | Standard Guide for Laboratory Immersion Corrosion Testing of Metals |
ASTM G 46 : 1994 : R2018 | Standard Guide for Examination and Evaluation of Pitting Corrosion |
ASTM G 39 : 1999 : R2021 | Standard Practice for Preparation and Use of Bent-Beam Stress-Corrosion Test Specimens |
ASTM G 38 : 2001 : R2021 | Standard Practice for Making and Using C-Ring Stress-Corrosion Test Specimens |
ASTM G 5 : 2014 : R2021 | Standard Reference Test Method for Making Potentiodynamic Anodic Polarization Measurements |
ASTM E 8 : 2004 | Standard Test Methods for Tension Testing of Metallic Materials |
ASTM G 3 : 2014 | Standard Practice for Conventions Applicable to Electrochemical Measurements in Corrosion Testing |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.