BS 6582:2000
Current
The latest, up-to-date edition.
Continuously hot-dip lead alloy (terne) coated cold reduced carbon steel flat rolled products
Hardcopy , PDF
English
15-06-2000
Important note : Users cannot be edited or removed once added to your Multi user PDF.
Committees responsible
Foreword
1 Scope
2 Normative references
3 Terms and definitions
4 Designation
5 Information to be supplied by the purchaser
6 General requirements
7 Specific requirements
Annex A (normative) Methods for determination of coating
mass
Annex B (informative) Proposed text for contractual clauses
Table 1 - Characteristics
Table 2 - Coating mass
Defines the criteria for continuously hot-dip lead alloy (terne) coated cold reduced low carbon steel flat products in forming and drawing grades. Applicable to flat products between 0.4mm and 2.0mm thickness, and widths not exceeding 1 350mm, in sheet and strip.
| Committee |
ISE/109
|
| DevelopmentNote |
Supersedes 99/13312 DC and BS 6582(1985). (09/2005) Reviewed and confirmed by BSI, December 2011. (11/2011)
|
| DocumentType |
Standard
|
| Pages |
12
|
| PublisherName |
British Standards Institution
|
| Status |
Current
|
This British Standard specifies requirements for continuously hot-dip lead alloy (terne) coated cold reduced low carbon steel flat products in drawing and forming grades.
This standard applies to flat products from over 0.4 mm up to and including 2.0 mm thick and widths up to 1 350 mm, in strip and sheet. It applies to products with terne coatings having a nominal mass of 120 g/m2 and to commercial grade terne coating (CGT) having no specified coating mass but meeting the other requirements of this standard.
NOTE The products in this standard can be used for applications where suitability for soldering and cold forming are required and corrosion resistance is a principal factor. The coating mass specified and the thickness of the base material should be compatible with the desired service life and forming requirements.
| ISO 10275:2007 | Metallic materials Sheet and strip Determination of tensile strain hardening exponent |
| BS EN 10020:2000 | Definition and classification of grades of steel |
| BS EN 10021:2006 | General technical delivery conditions for steel products |
| BS EN 10131:2006 | Cold rolled uncoated and zinc or zinc-nickel electrolytically coated low carbon and high yield strength steel flat products for cold forming. Tolerances on dimensions and shape |
| BS EN 10079:2007 | Definition of steel products |
| BS EN 10130:2006 | Cold rolled low carbon steel flat products for cold forming. Technical delivery conditions |
| EURONORM 12 : 1955 | FOLDING TEST OF SHEET STEELS AND STRIPS WITH A THICKNESS OF LESS THAN 3 MM |
| ISO 10113:2006 | Metallic materials Sheet and strip Determination of plastic strain ratio |
| BS EN 10002-1:2001 | Tensile testing of metallic materials Method of test at ambient temperature |
| BS EN 10204:2004 | Metallic products. Types of inspection documents |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.