BS EN 61788-2:2007

Current

Current

The latest, up-to-date edition.

Superconductivity Critical current measurement. D.C. critical current of Nb3Sn composite superconductors

Available format(s)

Hardcopy , PDF

Language(s)

English

Published date

28-02-2007

€254.76
Excluding VAT

INTRODUCTION
1 Scope
2 Normative references
3 Terms and definitions
4 Principle
5 Requirements
6 Apparatus
   6.1 Reaction mandrel material
   6.2 Reaction mandrel construction
   6.3 Measurement mandrel material
   6.4 Measurement mandrel construction
   6.5 Measurement set up
7 Specimen preparation
   7.1 Specimen mounting for reaction heat treatment
   7.2 Reaction heat treatment
   7.3 Specimen mounting for measurement
   7.4 Specimen bonding
8 Measurement procedure
9 Precision and accuracy of the test method
   9.1 Critical current
   9.2 Temperature
   9.3 Magnetic field
   9.4 Specimen support structure
   9.5 Specimen protection
10 Calculation of results
   10.1 Critical current criteria
   10.2 n-value (optional calculation, refer to A.7.2)
11 Test report
   11.1 Identification of test specimen
   11.2 Report of I[c] values
   11.3 Report of test conditions
Annex A (informative) Additional information relating to
        Clauses 1 to 10
Annex B (informative) Strain effect of Nb[3]Sn conductors
Annex C (informative) Self-field effect
Annex D (normative) One-mandrel method
Annex ZA (normative) Normative references to international
         publications with their corresponding European
         publications
Bibliography

Provides a test method for the determination of the d.c. critical current of Nb[3]Sn composite superconductors which are fabricated by either the bronze process or the internal tin diffusion process and have a copper/non-copper ratio larger than 0,2.

Committee
W/-
DocumentType
Standard
Pages
40
PublisherName
British Standards Institution
Status
Current
Supersedes

This part of IEC 61788 covers a test method for the determination of the d.c. critical current of Nb3Sn composite superconductors which are fabricated by either the bronze process or the internal tin diffusion process and have a copper/non-copper ratio larger than 0,2. This method is intended for use with superconductors which have critical currents of less than 1 000 A and n-values larger than 12 under standard test conditions and at magnetic fields of less than or equal to 0,7 times the upper critical magnetic field. The test specimen is immersed in a liquid helium bath at a known temperature during testing. The Nb3Sn composite test conductor has a monolithic structure with a total round-cross-sectional area that is less than 2 mm2. The specimen geometry used in this test method is an inductively coiled specimen. Deviations from this test method which are allowed for routine tests and other specific restrictions are given in this standard. Nb3Sn conductors with critical currents above 1 000 A or total cross-sectional areas greater than 2 mm2 can be measured with the present method with an anticipated reduction in precision and a more significant self-field effect (see Annex C). Other, more specialized, specimen test geometries may be more appropriate for larger conductor testing which have been omitted from this present standard for simplicity and to retain precision. The test method given in this standard should in principle apply to Nb3Sn composite wires fabricated by any other process. This method is also expected to apply to other superconducting composite wires after some appropriate modifications.

Standards Relationship
DIN EN 61788-2 : 2007 Identical
SN EN 61788-2 : 1999 Identical
IEC 61788-2:2006 Identical
NF EN 61788-2 : 2007 Identical
UNE-EN 61788-2:2000 Identical
I.S. EN 61788-2:2007 Identical
EN 61788-2:2007 Identical
NBN EN 61788-2 : 2007 Identical
EN 62020:1998/A1:2005 Identical

IEC 61788-1:2006 Superconductivity - Part 1: Critical current measurement - DC critical current of Nb-Ti composite superconductors
IEC 60050-815:2015 International Electrotechnical Vocabulary (IEV) - Part 815: Superconductivity
EN 61788-1:2007 Superconductivity - Part 1: Critical current measurement - DC critical current of Nb-Ti composite superconductors
IEC 60050-121:1998 International Electrotechnical Vocabulary (IEV) - Part 121: Electromagnetism

Access your standards online with a subscription

Features

  • Simple online access to standards, technical information and regulations.

  • Critical updates of standards and customisable alerts and notifications.

  • Multi-user online standards collection: secure, flexible and cost effective.