BS EN ISO 10309:2016
Current
The latest, up-to-date edition.
Metallic coatings. Porosity tests. Ferroxyl test
Hardcopy , PDF
English
30-04-2016
Important note : Users cannot be edited or removed once added to your Multi user PDF.| Committee |
STI/33
|
| DocumentType |
Standard
|
| Pages |
12
|
| PublisherName |
British Standards Institution
|
| Status |
Current
|
This International Standard specifies a method of revealing pores or other discontinuities, when testing metallic coatings, that are not visibly affected by ferricyanide and chloride ions during the test period and that are cathodic to iron and steel. This method is especially useful for thick, hard chromium coatings used for wear resistance.
NOTE 1 With some coating materials a very thin layer is dissolved by the sodium chloride solution during a 10 minute application period (see 5.2.3). The impact of such dissolution is that potential porosity, i.e. pores that have been covered over by very thin layers, are sometimes re-exposed. Experience has shown that such potential porosity is frequently re-exposed during actual service.
| Standards | Relationship |
| EN ISO 10309:2016 | Identical |
| ISO 10309:1994 | Identical |
| ISO 3696:1987 | Water for analytical laboratory use — Specification and test methods |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.