BS EN ISO 75-2:2013

Foreword
Introduction
1 Scope
2 Normative references
3 Terms and definitions
4 Principle
5 Apparatus
6 Test specimens
7 Conditioning
8 Procedure
9 Expression of results
10 Precision
11 Test report
Annex A (informative) - Precision
Bibliography

Describes three methods, using different values of constant flexural stress, that can be used for the determination of the temperature of deflection under load of plastics (including filled plastics and fibre-reinforced plastics in which the fibre length, prior to processing is up to 7,5 mm) and ebonite: - method A, using a flexural stress of 1,80 MPa; - method B, using a flexural stress of 0,45 MPa; - method C, using a flexural stress of 8,00 MPa.

This part of ISO75 specifies three methods, using different values of constant flexural stress, which can be used for the determination of the temperature of deflection under load of plastics (including filled plastics and fibre-reinforced plastics in which the fibre length, prior to processing, is up to 7,5mm) and ebonite:

• methodA, using a flexural stress of 1,80MPa;

• methodB, using a flexural stress of 0,45MPa;

• methodC, using a flexural stress of 8,00MPa.

The standard deflection, Δs, used to determine the temperature of deflection under load corresponds to a flexural-strain increase, Δε_f, defined in this part of ISO75. The initial flexural strain due to the loading of the specimen at room temperature is neither specified nor measured in this part of ISO75. The ratio of this flexural-strain increase to the initial flexural strain depends on the modulus of elasticity, at room temperature, of the material under test. This method is, therefore, only suitable for comparing the temperatures of deflection of materials with similar room-temperature elastic properties.

NOTE1 The methods give better reproducibility with amorphous plastics than with semi-crystalline ones. With some materials, it can be necessary to anneal the test specimens to obtain reliable results. Annealing procedures, if used, generally result in an increase in the temperature of deflection under load (see 6.6).

NOTE2 For additional information, see ISO75-1:2013, Clause1.