BS ISO 6721-4:2019

This document describes a forced, non-resonance method for determining the components of the tensile complex modulus E* of polymers at frequencies typically in the range 0,01 Hz to 100 Hz.

1 This document describes a forced, non-resonance method for determining the components of the tensile complex modulus E* of polymers at frequencies typically in the range 0,01Hz to 100Hz. NOTE Higher frequency measurements can be made, but significant errors in the dynamic properties measured are likely to result (see 10.2.2 and 10.2.3).The method is suitable for measuring dynamic storage moduli in the range 0,01GPa to 5GPa. Although materials with moduli outside this range can be studied, alternative modes of deformation are intended to be used for higher accuracy [i.e. a shear mode for G?5GPa (see ISO6721-3 or ISO6721-5)].This method is particularly suited to the measurement of loss factors and can therefore be conveniently used to study the variation of dynamic properties with temperature and frequency through most of the glass-rubber relaxation region (see ISO6721-1). The availability of data determined over wide ranges of both frequency and temperature enables master plots to be derived, using frequency-temperature shift procedures, which display dynamic properties over an extended frequency range at different temperatures.