CEN/TS 15863:2012

Foreword
Introduction
1 Scope
2 Normative references
3 Terms and definitions
4 Principle
5 Reagents
6 Equipment
7 Sample preparation
8 Procedure
9 Calculations
10 Documentation and test report
11 Test performance
Annex A (informative) - Identification of release
        mechanisms and use of test results
Annex B (informative) - Examples of data about
        the L/A ratio
Annex C (informative) - Process map for CEN/TS 15863
Bibliography

This document is applicable for determining the leaching behaviour of monolithic wastes under dynamic conditions. The test is performed under fixed experimental conditions in this document. This test is aimed at determining the release as a function of time of inorganic constituents from a monolithic waste, when it is put into contact with an aqueous solution (leachant).This Dynamic Monolithic Leaching Test (DMLT) is a parameter specific test as specified in EN 12920 and is therefore not aimed at simulating real situations. The application of this test method alone is not sufficient for the determination of the detailed leaching behaviour of a monolithic waste under specified conditions.In the framework of EN 12920 and in combination with additional chemical information, the test results are used to identify the leaching mechanisms and their relative importance. The intrinsic properties can be used to predict the release of constituents at a given time frame, in order to assess the leaching behaviour of monolithic waste materials, placed in different situations or scenarios (including disposal and recycling scenarios).The test method applies to regularly shaped test portions of monolithic wastes with minimum dimensions of 40 mm in all directions, that are assumed to maintain their integrity over a time frame relevant for the considered scenario. The test method applies to test portions for which the geometric surface area can be determined with the help of simple geometric equations. The test method applies to low permeable monolithic materials.NOTE 1If, in order to comply with the requirements of regular shape, the test portion is prepared by cutting or coring, then new surfaces are exposed which can lead to change(s) in leaching properties. On the other hand if the test portion is prepared by moulding, the surface will be dependent to the type of mould and the conditions of storage. If the intention is to evaluate the behaviour of the material core, the