DIN 17022-3:1989-04
Current
The latest, up-to-date edition.
HEAT TREATMENT OF FERROUS MATERIALS - HEAT TREATMENT METHODS - CASE HARDENING
Hardcopy , PDF
English, German
01-04-1989
1 Scope and field of application
2 Terminology
3 Principles of case hardening
4 Indication of case-hardened condition in documentation
5 Procedure
5.1 Workpiece preparation and pretreatment
5.1.1 Workpiece preparation
5.1.2 Stress relieving
5.1.3 Normalizing
5.1.4 Hardening and tempering
5.1.5 Preparation for local carburizing or
carbonitriding
5.1.6 Charging of workpieces
5.2 Heating to treatment temperature
5.3 Carburizing
5.3.1 Carburizing with constant carbon
potential
5.3.2 Carburizing with variable carbon
potential
5.3.3 Case depth
5.3.4 Carburizing in solid media (granulate)
5.3.5 Salt bath carburizing
5.3.6 Gas carburizing
5.3.6.1 Gas carburizing with carbon
potential control
5.3.6.2 Gas carburizing without
carbon potential control
5.4 Carbonitriding
5.4.1 Salt bath carbonitridingn the case of
gas carburizing
5.4.2 Gas carbonitriding
5.5 Quench hardening
5.5.1 General
5.5.2 Direct hardening
5.5.3 Single hardening
5.5.4 Double quench hardening
5.6 Sub-zero treatment
5.7 Tempering
6 Heat treatment media
6.1 Heating media
6.1.1 Liquid heating media
6.1.2 Gaseous heating media
6.1.3 Vacuum
6.2 Carburizing and carbonitriding media
6.2.1 Solid media (granulate)
6.2.2 Salt baths
6.2.3 Gases
6.2.3.1 Gases for carburizing
6.2.3.2 Gases for carbonitriding
6.3 Cooling and quenching media
6.3.1 Liquid quenching media
6.3.2 Gaseous cooling media
6.3.3 Cooling media for sub-zero treatment
7 Instructions on equipment used in heat treatment
7.1 Heat treatment furnace
7.2 Cooling and quenching equipment
7.3 Sub-zero treatment equipment
8 Defects in heat treated workpieces
9 Heat treatment as a criterion in design
10 Instructions on straightening
11 Inspection of heat treated workpieces
Appendix A
A.1 - Recommended surface carbon content for low
retained austenite levels
A.2 - Relationship between carbon potential and gas
composition in the case of gas carburizing
A.3 - Local case hardening
Standards and other documents referred to
This standard is included in DIN HDBK 218. Gives criteria for case hardening procedure and gives instructions on the case hardening of steel workpieces and tools.
DocumentType |
Standard
|
Pages |
22
|
PublisherName |
German Institute for Standardisation (Deutsches Institut für Normung)
|
Status |
Current
|
DIN 50192:1977-05 | DETERMINATION OF DEPTH OF DECARBURIZATION |
DIN 50103-1:1984-03 | TESTING OF METALLIC MATERIALS; ROCKWELL HARDNESS TEST; C, A, B, F SCALES |
DIN 17014-1:1988-08 | HEAT TREATMENT OF FERROUS MATERIALS - TERMINOLOGY |
DIN 1654-3:1989-10 | COLD HEADING AND COLD EXTRUDING STEELS - TECHNICAL DELIVERY CONDITIONS FOR CASE HARDENING STEELS |
DIN 50150:2000-10 | TESTING OF METALLIC MATERIALS - CONVERSION OF HARDNESS VALUES |
DIN 50601:1985-08 | METALLOGRAPHIC TEST METHODS; DETERMINATION OF THE FERRITIC OR AUSTENITIC GRAIN SIZE OF STEELS AND FERROUS MATERIALS |
DIN 50190-1:1978-11 | HARDNESS DEPTH OF HEAT-TREATED PARTS; DETERMINATION OF THE EFFECTIVE DEPTH OF CARBURIZED AND HARDENED CASES |
DIN 17350:1980-10 | TOOL STEELS - TECHNICAL CONDITIONS OF DELIVERY |
DIN 1651:1988-04 | FREE-CUTTING STEELS - TECHNICAL DELIVERY CONDITIONS |
DIN 50133:1985-02 | TESTING OF METALLIC MATERIALS; VICKERS HARDNESS TEST, HV 0.2 TO HV 100 |
DIN 50103-2:1984-03 | TESTING OF METALLIC MATERIALS; ROCKWELL HARDNESS TEST; N AND T SCALES |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.