EN 2828:1993
Current
The latest, up-to-date edition.
Aerospace series - Adhesion test for metallic coatings by burnishing
26-02-1993
Foreword
1 Scope
2 Normative references
3 Test equipment
4 Procedure
5 Fault sanction
6 Test report
This standard specifies the test method to determine the adhesion of coatings by burnishing. It applies to coatings of ductile metals such as cadmium, copper or silver with a hardness of less than 250 HV and thickness of less than or equal to 40 micrometre. It is applicable whenever referenced.
| Committee |
ASD-STAN
|
| DevelopmentNote |
Supersedes PREN 2828. (11/2003)
|
| DocumentType |
Standard
|
| PublisherName |
Comite Europeen de Normalisation
|
| Status |
Current
|
| Supersedes |
| Standards | Relationship |
| PN EN 2828 : 1999 | Identical |
| NF EN 2828 : 1993 | Identical |
| BS EN 2828:1993 | Identical |
| NBN EN 2828 : 1993 | Identical |
| DIN EN 2828:1993-04 | Identical |
| UNE-EN 2828:1996 | Identical |
| NS EN 2828 : 1ED 1993 | Identical |
| SNV DIN EN 2828 : 1993 | Identical |
| I.S. EN 2828:1993 | Identical |
| UNI EN 2828 : 1993 | Identical |
| UNE-EN 2828:1993 | Identical |
| 92/75739 DC : DRAFT APR 1992 | PREN 3765 - AEROSPACE SERIES - ELECTROLYTIC SILVER PLATING FOR GENERAL USE - STEELS, HEAT RESISTING ALLOYS, COPPER AND COPPER ALLOYS |
| BS EN 2535:2011 | Aerospace series. Vacuum deposition of cadmium |
| PREN 2133 : 200P1 | AEROSPACE SERIES - CADMIUM PLATING OF STEELS WITH SPECIFIED TENSILE STRENGTH <= 1450 MPA, COPPER, COPPER ALLOYS AND NICKEL ALLOYS |
| I.S. EN 2535:2011 | AEROSPACE SERIES - VACUUM DEPOSITION OF CADMIUM |
| PREN 3765 : 200P1 | AEROSPACE SERIES - ELECTROLYTIC SILVER PLATING FOR GENERAL USE - STEELS, HEAT RESISTING ALLOYS, COPPER AND COPPER ALLOYS |
| EN 2133:2010 | Aerospace series - Cadmium plating of steels with specified tensile strength ≤ 1 450 MPa, copper, copper alloys and nickel alloys |
| 93/706720 DC : 0 | PREN 2535 - AEROSPACE SERIES - VACUUM DEPOSITION OF CADMIUM |
| PREN 2535 : 200P1 | AEROSPACE SERIES - VACUUM DEPOSITION OF CADMIUM |
| I.S. EN 2786:2008 | AEROSPACE SERIES - ELECTROLYTIC SILVER PLATING OF FASTENERS |
| I.S. EN 2133:2010 | AEROSPACE SERIES - CADMIUM PLATING OF STEELS WITH SPECIFIED TENSILE STRENGTH <= 1450 MPA, COPPER, COPPER ALLOYS AND NICKEL ALLOYS |
| UNI EN 2133 : 2011 | AEROSPACE SERIES - CADMIUM PLATING OF STEELS WITH SPECIFIED TENSILE STRENGTH <= 1450 MPA, COPPER, COPPER ALLOYS AND NICKEL ALLOYS |
| DIN EN 3765:1997-09 (Draft) | AEROSPACE SERIES - ELECTROLYTIC SILVER PLATING FOR GENERAL USE - STEELS, HEAT RESISTING ALLOYS, COPPER AND COPPER ALLOYS |
| 09/30207944 DC : 0 | BS EN 2133 - AEROSPACE SERIES - CADMIUM PLATING OF STEELS WITH SPECIFIED TENSILE STRENGTH <= 1450 MPA, COPPER, COPPER ALLOYS AND NICKEL ALLOYS |
| BS EN 2786:2008 | Aerospace series. Electrolytic silver plating of fasteners |
| PREN 2786 : 200P1 | AEROSPACE SERIES - ELECTROLYTIC SILVER PLATING OF FASTENERS |
| 16/30339916 DC : 0 | BS EN 2133 - AEROSPACE SERIES - CADMIUM PLATING OF STEELS WITH SPECIFIED TENSILE STRENGTH <= 1450 MPA, COPPER, COPPER ALLOYS AND NICKEL ALLOYS |
| 17/30366369 DC : 0 | BS EN 2133 AEROSPACE SERIES - CADMIUM PLATING OF STEELS WITH SPECIFIED TENSILE STRENGTH <= 1450 MPA, COPPER, COPPER ALLOYS AND NICKEL ALLOYS |
| BS EN 2133:2010 | Aerospace series. Cadmium plating of steels with specified tensile strength ≤ 1450 MPa, copper, copper alloys and nickel alloys |
| EN 2786:2008 | Aerospace series - Electrolytic silver plating of fasteners |
| EN 2535:2011 | Aerospace series - Vacuum deposition of cadmium |
| UNI EN 2535 : 2012 | AEROSPACE SERIES - VACUUM DEPOSITION OF CADMIUM |
| NF EN 2535 : 2012 | AEROSPACE SERIES - VACUUM DEPOSITION OF CADMIUM |
| ISO 2080:2008 | Metallic and other inorganic coatings Surface treatment, metallic and other inorganic coatings Vocabulary |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.