IEC 60404-6:2003

FOREWORD
1 Scope
2 Normative references
3 Terms and definitions
4 General principles of measurement
5 Temperature measurements
6 Measurement of the relative amplitude permeability
  and the AC magnetization curve
7 Measurement of the specific total loss by the
  wattmeter method
8 Uncertainties
9 Test report
Annex A (informative) - Guidance on requirements for
        windings and instrumentation in order to
        minimise additional losses
Annex B (informative) - Digital sampling technique for
        the determination of magnetic properties and
        numerical air flux compensation
Annex C (informative) - Sinusoidal waveform control by
        digital means
Bibliography

Specifies methods for the measurement of a.c. magnetic properties of materials in the frequency range 20 Hz to 200 kHz other than electrical steels and soft ferrites. The materials covered by this part of IEC 60404 include those speciality alloys listed in IEC 60404-8-6, amorphous and nanocrystalline materials, pressed and sintered and metal injection moulded parts such as are listed in IEC 60404-8-9, cast parts and magnetically soft composite materials.The object of this part is to define the general principles and the technical details of the measurement of the magnetic properties of magnetically soft materials by means of ring methods. For materials supplied in powder form, a ring test specimen is formed by the appropriate pressing method for that material.DC magnetic measurements on magnetically soft materials shall be made in accordance with the ring method of IEC 60404-4. The determinations of the magnetic characteristics of magnetically soft components shall be made in accordance with IEC 62044-3.Normally, the measurements shall be made at an ambient temperature of (23 ± 5) °C on ring test specimens which have first been magnetized, then demagnetized. Measurements can be made over other temperature ranges by agreement between supplier and purchaser.The scope of the second edition has been extended to include all magnetically soft materials except ferrites.The contents of the corrigendum of February 2009 have been included in this copy.