ISO 7539-1:2012
Current
The latest, up-to-date edition.
Corrosion of metals and alloys — Stress corrosion testing — Part 1: General guidance on testing procedures
Hardcopy , PDF , PDF 3 Users , PDF 5 Users , PDF 9 Users
English, French
14-12-2012
ISO 7539-1:2012 describes the general considerations that apply when designing and conducting tests to assess susceptibility of metals to stress corrosion.
ISO 7539-1:2012 also gives some general guidance on the selection of test methods.
Committee |
ISO/TC 156
|
DevelopmentNote |
Supersedes ISO/DIS 7539-1. (12/2012)
|
DocumentType |
Standard
|
Pages |
20
|
PublisherName |
International Organization for Standardization
|
Status |
Current
|
Supersedes |
Standards | Relationship |
NF EN ISO 7539-1 : 2013 | Identical |
UNE-EN ISO 7539-1:2013 | Identical |
NBN EN ISO 7539-1 : 2013 | Identical |
NEN EN ISO 7539-1 : 2013 | Identical |
NS EN ISO 7539-1 : 2012 | Identical |
I.S. EN ISO 7539-1:2012 | Identical |
PN EN ISO 7539-1 : 2013 | Identical |
SN EN ISO 7539-1:2013 | Identical |
UNI EN ISO 7539-1 : 2013 | Identical |
BS EN ISO 7539-1:2012 | Identical |
EN ISO 7539-1:2012 | Identical |
DIN EN ISO 7539-1:2013-04 | Identical |
BS 6980-1(1988) : 1988 AMD 8715 | Identical |
SAC GB/T 15970.1 : 1995 | Identical |
DIN EN ISO 7539-10:2015-03 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 10: REVERSE U-BEND METHOD (ISO 7539-10:2013) |
I.S. EN ISO 11782-2:2008 | CORROSION OF METALS AND ALLOYS - CORROSION FATIGUE TESTING - PART 2: CRACK PROPAGATION TESTING USING PRECRACKED SPECIMENS |
ONORM EN ISO 7539-6 : 2012 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 6: PREPARATION AND USE OF PRECRACKED SPECIMENS FOR TESTS UNDER CONSTANT LOAD OR CONSTANT DISPLACEMENT (ISO 7539-6:2011) |
DIN EN ISO 11782-2:2008-08 | Corrosion of metals and alloys - Corrosion fatigue testing - Part 2: Crack propagation testing using precracked specimens (ISO 11782-2:1998) |
DIN EN ISO 15324:2008-07 | Corrosion of metals and alloys - Evaluation of stress corrosion cracking by the drop evaporation test (ISO 15324:2000) |
DIN EN ISO 11782-1:2008-08 | Corrosion of metals and alloys - Corrosion fatigue testing - Part 1: Cycles to failure testing (ISO 11782-1:1998) |
17/30337655 DC : 0 | BS ISO 21153 - CORROSION OF METALS AND ALLOYS - MEASUREMENT OF ENVIRONMENTALLY ASSISTED SMALL CRACK GROWTH RATE |
07/30174321 DC : 0 | BS EN ISO 11130 - CORROSION OF METALS AND ALLOYS - ALTERNATE IMMERSION TEST IN SALT SOLUTION |
BS ISO 11782-2 : 1998 | CORROSION OF METAL AND ALLOYS - CORROSION FATIGUE TESTING - CRACK PROPAGATION TESTING USING PRECRACKED SPECIMENS |
I.S. EN ISO 7539-9:2008 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 9: PREPARATION AND USE OF PRE-CRACKED SPECIMENS FOR TESTS UNDER RISING LOAD OR RISING DISPLACEMENT |
UNI EN ISO 7539-6 : 2011 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 6: PREPARATION AND USE OF PRECRACKED SPECIMENS FOR TESTS UNDER CONSTANT LOAD OR CONSTANT DISPLACEMENT |
BS EN ISO 11130:2018 | Corrosion of metals and alloys. Alternate immersion test in salt solution |
UNI EN ISO 7539-9 : 2008 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 9: PREPARATION AND USE OF PRE-CRACKED SPECIMENS FOR TESTS UNDER RISING LOAD OR RISING DISPLACEMENT |
UNI EN ISO 11782-2 : 2008 | CORROSION OF METALS AND ALLOYS - CORROSION FATIGUE TESTING - PART 2: CRACK PROPAGATION TESTING USING PRECRACKED SPECIMENS |
BS EN ISO 7539-6:2011 | Corrosion of metals and alloys. Stress corrosion testing Preparation and use of precracked specimens for tests under constant load or constant displacement |
I.S. EN ISO 11782-1:2008 | CORROSION OF METALS AND ALLOYS - CORROSION FATIGUE TESTING - PART 1: CYCLES TO FAILURE TESTING |
UNE-EN ISO 11114-4:2017 | Transportable gas cylinders - Compatibility of cylinder and valve materials with gas contents - Part 4: Test methods for selecting steels resistant to hydrogen embrittlement (ISO 11114-4:2017) |
BS EN ISO 7539-3:1995 | Corrosion of metals and alloys. Stress corrosion testing Preparation and use of U-bend specimens |
DIN EN ISO 11114-4:2017-09 | TRANSPORTABLE GAS CYLINDERS - COMPATIBILITY OF CYLINDER AND VALVE MATERIALS WITH GAS CONTENTS - PART 4: TEST METHODS FOR SELECTING STEELS RESISTANT TO HYDROGEN EMBRITTLEMENT (ISO 11114-4:2017) |
BS EN ISO 7539-9:2008 | Corrosion of metals and alloys. Stress corrosion testing Preparation and use of pre-cracked specimens for tests under rising load or rising displacement |
DIN EN ISO 7539-6:2012-01 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 6: PREPARATION AND USE OF PRECRACKED SPECIMENS FOR TESTS UNDER CONSTANT LOAD OR CONSTANT DISPLACEMENT (ISO 7539-6:2011) |
ISO 9591:2004 | Corrosion of aluminium alloys — Determination of resistance to stress corrosion cracking |
BS 6980-5(1990) : 1990 AMD 1995 | STRESS CORROSION TESTING - METHOD FOR THE PREPARATION AND USE OF C-RING SPECIMENS |
BS EN ISO 11782-1:2008 | Corrosion of metals and alloys. Corrosion fatigue testing Cycles to failure testing |
BS ISO 11782-1 : 1998 | CORROSION OF METAL AND ALLOYS - CORROSION FATIGUE TESTING - CYCLES TO FAILURE TESTING |
I.S. EN ISO 7539-10:2014 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 10: REVERSE U-BEND METHOD (ISO 7539-10:2013) |
EN ISO 7539-6:2011 | Corrosion of metals and alloys - Stress corrosion testing - Part 6: Preparation and use of precracked specimens for tests under constant load or constant displacement (ISO 7539-6:2011) |
ISO 21601:2013 | Corrosion of metals and alloys — Guidelines for assessing the significance of stress corrosion cracks detected in service |
I.S. EN ISO 7539-6:2011 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 6: PREPARATION AND USE OF PRECRACKED SPECIMENS FOR TESTS UNDER CONSTANT LOAD OR CONSTANT DISPLACEMENT (ISO 7539-6:2011) |
I.S. EN ISO 15324:2008 | CORROSION OF METALS AND ALLOYS - EVALUATION OF STRESS CORROSION CRACKING BY THE DROP EVAPORATION TEST |
I.S. EN ISO 11114-4:2017 | TRANSPORTABLE GAS CYLINDERS - COMPATIBILITY OF CYLINDER AND VALVE MATERIALS WITH GAS CONTENTS - PART 4: TEST METHODS FOR SELECTING STEELS RESISTANT TO HYDROGEN EMBRITTLEMENT (ISO 11114-4:2017) |
PD 6493:1991 | Guidance on methods for assessing the acceptability of flaws in fusion welded structures |
BS EN ISO 7539-7:2005 | Corrosion of metals and alloys. Stress corrosion testing Method for slow strain rate testing |
BS EN ISO 11782-2:2008 | Corrosion of metals and alloys. Corrosion fatigue testing Crack propagation testing using precracked specimens |
13/30237862 DC : 0 | BS ISO 16540 - CORROSION OF METALS AND ALLOYS - METHODOLOGY FOR DETERMINING THE RESISTANCE OF METALS TO STRESS CORROSION CRACKING USING THE FOUR-POINT BEND METHOD |
BS ISO 21601:2013 | Corrosion of metals and alloys. Guidelines for assessing the significance of stress corrosion cracks detected in service |
BS 6980-6(1990) : AMD 8734 | STRESS CORROSION TESTING - METHOD FOR THE PREPARATION AND USE OF PRE-CRACKED SPECIMENS |
ISO 7539-2:1989 | Corrosion of metals and alloys Stress corrosion testing Part 2: Preparation and use of bent-beam specimens |
ONORM EN ISO 7539-10 : 2015 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 10: REVERSE U-BEND METHOD (ISO 7539-10:2013) |
EN ISO 7539-10:2014 | Corrosion of metals and alloys - Stress corrosion testing - Part 10: Reverse U-bend method (ISO 7539-10:2013) |
BS EN ISO 7539-10:2014 | Corrosion of metals and alloys. Stress corrosion testing Reverse U-bend method |
BS ISO 15324 : 2000 | CORROSION OF METALS AND ALLOYS - EVALUATION OF STRESS CORROSION CRACKING BY THE DROP EVAPORATION TEST |
BS ISO 7539-10 : 2013 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 10: REVERSE U-BEND METHOD |
DIN EN ISO 7539-7:2005-05 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 7: METHOD FOR SLOW STRAIN RATE TESTING |
BS EN ISO 15324:2008 | Corrosion of metals and alloys. Evaluation of stress corrosion cracking by the drop evaporation test |
NACE TM 03 16 : 2016 | FOUR-POINT BEND TESTING OF MATERIALS FOR OIL AND GAS APPLICATIONS |
03/104505 DC : DRAFT FEB 2003 | BS ISO 11114-4 - TRANSPORTABLE GAS CYLINDERS - COMPATIBILITY OF CYLINDER AND VALVE MATERIALS WITH GAS CONTENTS - PART 4: TEST METHODS FOR SELECTING METALLIC MATERIALS RESISTANT TO HYDROGEN EMBRITTLEMENT |
15/30288130 DC : 0 | BS EN ISO 11114-4 - TRANSPORTABLE GAS CYLINDERS - COMPATIBILITY OF CYLINDER AND VALVE MATERIALS WITH GAS CONTENTS - PART 4: TEST METHODS FOR SELECTING STEELS RESISTANT TO HYDROGEN EMBRITTLEMENT |
ISO 16540:2015 | Corrosion of metals and alloys Methodology for determining the resistance of metals to stress corrosion cracking using the four-point bend method |
11/30243821 DC : DRAFT JULY 2011 | BS ISO 7539-10 - CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 10: REVERSE U-BEND METHOD |
03/314809 DC : DRAFT SEP 2003 | EN ISO 13680 - PETROLEUM AND NATURAL GAS INDUSTRIES - CORROSION-RESISTANT ALLOY SEAMLESS TUBES FOR USE AS CASING, TUBING AND COUPLING STOCK - TECHNICAL DELIVERY CONDITIONS |
DIN EN ISO 7539-9:2008-08 | Corrosion of metals and alloys - Stress corrosion testing - Part 9: Preparation and use of pre-cracked specimens for tests under rising load or rising displacement (ISO 7539-9:2003) |
BS ISO 16540:2015 | Corrosion of metals and alloys. Methodology for determining the resistance of metals to stress corrosion cracking using the four-point bend method |
05/30139447 DC : DRAFT SEP 2005 | ISO 21601 - GUIDELINES FOR ASSESSING THE SIGNIFICANCE OF STRESS CORROSION CRACKS DETECTED IN SERVICE |
11/30219244 DC : DRAFT SEP 2011 | BS ISO 21601 - CORROSION OF METALS AND ALLOYS - GUIDELINES FOR ASSESSING THE SIGNIFICANCE OF STRESS CORROSION CRACKS DETECTED IN SERVICE |
NF EN ISO 7539-6 : 2011 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 6: PREPARATION AND USE OF PRECRACKED SPECIMENS FOR TESTS UNDER CONSTANT LOAD OR CONSTANT DISPLACEMENT |
UNE-EN ISO 7539-10:2015 | Corrosion of metals and alloys - Stress corrosion testing - Part 10: Reverse U-bend method (ISO 7539-10:2013) |
UNI EN ISO 11130 : 2010 | CORROSION OF METALS AND ALLOYS - ALTERNATE IMMERSION TEST IN SALT SOLUTION |
ISO 7539-6:2011 | Corrosion of metals and alloys Stress corrosion testing Part 6: Preparation and use of precracked specimens for tests under constant load or constant displacement |
ISO 7539-7:2005 | Corrosion of metals and alloys — Stress corrosion testing — Part 7: Method for slow strain rate testing |
EN ISO 7539-9:2008 | Corrosion of metals and alloys - Stress corrosion testing - Part 9: Preparation and use of pre-cracked specimens for tests under rising load or rising displacement (ISO 7539-9:2003) |
EN ISO 11130:2018 | Corrosion of metals and alloys - Alternate immersion test in salt solution (ISO 11130:2017) |
I.S. EN ISO 11130:2018 | CORROSION OF METALS AND ALLOYS - ALTERNATE IMMERSION TEST IN SALT SOLUTION (ISO 11130:2017) |
UNE-EN ISO 7539-6:2012 | Corrosion of metals and alloys - Stress corrosion testing - Part 6: Preparation and use of precracked specimens for tests under constant load or constant displacement (ISO 7539-6:2011) |
BS EN ISO 7539-5:1995 | Corrosion of metals and alloys. Stress corrosion testing Method for the preparation and use of C-ring specimens |
ISO 7539-5:1989 | Corrosion of metals and alloys Stress corrosion testing Part 5: Preparation and use of C-ring specimens |
BS EN ISO 11114-4:2005 | Transportable gas cylinders. Compatibility of cylinder and valve materials with gas contents Test methods for selecting metallic materials resistant to hydrogen embrittlement |
ISO 11114-4:2017 | Transportable gas cylinders Compatibility of cylinder and valve materials with gas contents Part 4: Test methods for selecting steels resistant to hydrogen embrittlement |
ISO 7539-10:2013 | Corrosion of metals and alloys Stress corrosion testing Part 10: Reverse U-bend method |
ISO 7539-3:1989 | Corrosion of metals and alloys Stress corrosion testing Part 3: Preparation and use of U-bend specimens |
ISO 7539-9:2003 | Corrosion of metals and alloys Stress corrosion testing Part 9: Preparation and use of pre-cracked specimens for tests under rising load or rising displacement |
EN ISO 11782-1:2008 | Corrosion of metals and alloys - Corrosion fatigue testing - Part 1: Cycles to failure testing (ISO 11782-1:1998) |
EN ISO 11782-2:2008 | Corrosion of metals and alloys - Corrosion fatigue testing - Part 2: Crack propagation testing using precracked specimens (ISO 11782-2:1998) |
EN ISO 11114-4:2017 | Transportable gas cylinders - Compatibility of cylinder and valve materials with gas contents - Part 4: Test methods for selecting steels resistant to hydrogen embrittlement (ISO 11114-4:2017) |
EN ISO 7539-7 : 2005 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 7: METHOD FOR SLOW STRAIN RATE TESTING (ISO 7539-7:2005) |
EN ISO 7539-5 : 1995 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 5: PREPARATION AND USE OF C-RING SPECIMENS (ISO 7539-5:1989) |
EN ISO 7539-2 : 1995 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 2: PREPARATION AND USE ON BENT-BEAM SPECIMEN (ISO 7539-2:1989) |
EN ISO 7539-4 : 1995 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 4: PREPARATION AND USE OF UNIAXIALLY LOADED TENSION SPECIMENS |
EN ISO 7539-3 : 1995 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 3: PREPARATION AND USE OF U-BEND SPECIMENS |
EN ISO 15324:2008 | Corrosion of metals and alloys - Evaluation of stress corrosion cracking by the drop evaporation test (ISO 15324:2000) |
UNI EN ISO 11782-1 : 2008 | CORROSION OF METALS AND ALLOYS - CORROSION FATIGUE TESTING - PART 1: CYCLES TO FAILURE TESTING |
BS 6980-3(1990) : 1990 AMD 8712 | STRESS CORROSION TESTING - METHOD FOR THE PREPARATION AND USE OF U BEND SPECIMENS |
17/30346602 DC : 0 | BS EN ISO 11130 - CORROSION OF METALS AND ALLOYS - ALTERNATE IMMERSION TEST IN SALT SOLUTION |
I.S. EN ISO 7539-7:2005 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 7: METHOD FOR SLOW STRAIN RATE TESTING |
17/30363807 DC : 0 | BS EN ISO 7539-6 - CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 6: PREPARATION AND USE OF PRECRACKED SPECIMENS FOR TESTS UNDER CONSTANT LOAD OR CONSTANT DISPLACEMENT |
BS ISO 7539-9 : 2003 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 9: PREPARATION AND USE OF PRE-CRACKED SPECIMENS FOR TESTS UNDER RISING LOAD OR RISING DISPLACEMENT |
UNE-EN ISO 11130:2011 | Corrosion of metals and alloys - Alternate immersion test in salt solution (ISO 11130:2010) |
NF EN ISO 11130 : 2010 | CORROSION OF METALS AND ALLOYS - ALTERNATE IMMERSION TEST IN SALT SOLUTION |
DIN EN ISO 11130:2010-12 | CORROSION OF METALS AND ALLOYS - ALTERNATE IMMERSION TEST IN SALT SOLUTION |
UNI EN ISO 15324 : 2008 | CORROSION OF METALS AND ALLOYS - EVALUATION OF STRESS CORROSION CRACKING BY THE DROP EVAPORATION TEST |
DIN EN ISO 11114-4:2015-08 (Draft) | TRANSPORTABLE GAS CYLINDERS - COMPATIBILITY OF CYLINDER AND VALVE MATERIALS WITH GAS CONTENTS - PART 4: TEST METHODS FOR SELECTING STEELS RESISTANT TO HYDROGEN EMBRITTLEMENT (ISO 11114-4:2017) |
ISO 15324:2000 | Corrosion of metals and alloys Evaluation of stress corrosion cracking by the drop evaporation test |
ONORM EN ISO 7539-9 : 2008 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION TESTING - PART 9: PREPARATION AND USE OF PRE-CRACKED SPECIMENS FOR TESTS UNDER RISING LOAD OR RISING DISPLACEMENT |
ISO 4287:1997 | Geometrical Product Specifications (GPS) — Surface texture: Profile method — Terms, definitions and surface texture parameters |
ISO 7539-9:2003 | Corrosion of metals and alloys Stress corrosion testing Part 9: Preparation and use of pre-cracked specimens for tests under rising load or rising displacement |
ISO 15324:2000 | Corrosion of metals and alloys Evaluation of stress corrosion cracking by the drop evaporation test |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.