NBN EN 10327 : 2004

Foreword
1 Scope
2 Normative references
3 Terms and definitions
4 Classification and designation
   4.1 Classification
   4.2 Designation
5 Information to be supplied by the purchaser
   5.1 Mandatory information
   5.2 Options
6 Manufacturing process
7 Requirements
   7.1 Chemical composition
   7.2 Mechanical properties
   7.3 Coatings
   7.4 Coating finish
   7.5 Surface quality
   7.6 Surface treatment (surface protection)
   7.7 Freedom from coil breaks
   7.8 Stretcher strains
   7.9 Coating mass
   7.10 Adhesion of coating
   7.11 Surface condition
   7.12 Tolerances on dimensions and shape
   7.13 Suitability for further processing
8 Testing
   8.1 General
   8.2 Test units
   8.3 Number of tests
   8.4 Sampling
   8.5 Test methods
   8.6 Retests
9 Marking
10 Packing
11 Storage and transportation
12 Disputes
Annex A (normative) Reference method for determination of the zinc,
        zinc-aluminium and aluminium-zinc coating mass
Annex B (normative) Reference method for determination of the
        aluminium-silicon coating mass
Annex C (normative) Method for determination of the mass of the
        Al-Fe-Si alloy layer
Bibliography

Describes requirements for continuously hot-dip coated products made of low carbon steels for cold forming coated with zinc (Z), zinc-iron alloy (ZF), zinc-aluminium alloy (ZA), aluminium-zinc alloy (AZ) and aluminium-silicon alloy (AS) with thicknesses of 0,35 mm to 3,0 mm unless otherwise agreed.