SAE AMS 03-27 : S2017
Current
The latest, up-to-date edition.
ELECTRO-DEPOSITION OF NICKEL FOR ENGINEERING PURPOSES
Hardcopy , PDF
English
19-10-2017
Important note : Users cannot be edited or removed once added to your Multi user PDF.
1. SCOPE
2. WARNING
3. NORMATIVE REFERENCES
4. DEFINITIONS
5. INFORMATION TO BE SUPPLIED TO THE
PROCESSOR
6. PROCESS CONTROL
7. PREPARATION FOR COATING
8. RECLAMATION OF WORN OR OVER-MACHINED
ITEMS
9. CONDITION OF SUBSTRATE (PROCESS REQUIREMENTS)
10. MINIMIZING THE RISK OF HYDROGEN EMBRITTLEMENT
OF STEEL ITEMS
11. STRESS RELIEF
12. INTRODUCTION TO SURFACE COMPRESSIVE STRESSES
13. PREPARATION FOR PLATING
14. ELECTRO-DEPOSITION OF NICKEL
15. POST PLATING HEAT TREATMENT
16. INSPECTION, SAMPLING AND TESTING
17. TREATMENT OF ITEMS REJECTED DURING INSPECTION
AND TEST
18. NOTES
ANNEX A - NICKEL PLATING SOLUTIONS AND CONDITIONS
ANNEX B - THE ANALYSIS OF NICKEL PLATING SOLUTIONS
ANNEX C - ADDITIONAL REQUIREMENTS AND INFORMATION
ANNEX D - ADHESION TESTS
ANNEX E - CHEMICAL METHODS OF STRIPPING NICKEL
DEPOSITS
This SAE Standard specifies the requirements for the nickel-plating of ferrous metals, copper alloys, aluminum alloys and zinc alloys for one or more of the following purposes: athe production of wear-resistant surfaces; bthe building up of worn or over-machined surfaces; ccorrosion resistance; dto provide an undercoat for subsequent deposits, e.g., chromium.
| Committee |
AMS-B
|
| DevelopmentNote |
Supersedes DEFSTAN 03-27/3(2005). (05/2015)
|
| DocumentType |
Standard
|
| Pages |
28
|
| ProductNote |
THIS STANDARD IS NOW STABILIZED
|
| PublisherName |
SAE International
|
| Status |
Current
|
| Supersedes |
| BS 6200-3.22.1:1992 | Sampling and analysis of iron, steel and other ferrous metals. Methods of analysis. Determination of nitrogen Steel: volumetric method |
| BS 1752:1983 | Specification for laboratory sintered or fritted filters including porosity grading |
| BS EN ISO 3696:1995 | Water for analytical laboratory use. Specification and test methods |
| DEFSTAN 03-14/4(2008) : 2008 | ELECTRODEPOSITION OF CHROMIUM FOR ENGINEERING PURPOSES |
| BS EN ISO 6507-1:2005 | Metallic materials. Vickers hardness test Test method |
| DEFSTAN 03-4/6(2011) : 2011 | THE PRE-TREATMENT AND PROTECTION OF STEEL ITEMS OF SPECIFIED MAXIMUM TENSILE STRENGTH EXCEEDING 1450 MPA |
| SAE AMS 03-14 : 2015 | ELECTRODEPOSITION OF CHROMIUM FOR ENGINEERING PURPOSES |
| DEFSTAN 03-2/6(2011) : 2011 | CLEANING AND PREPARATION OF METAL SURFACES |
| SAE AMS 03-2 : 2017 | CLEANING AND PREPARATION OF METAL SURFACES |
| SAE AMS03-4A : 2015(S2017) | THE PRE-TREATMENT AND PROTECTION OF STEEL ITEMS OF SPECIFIED MAXIMUM TENSILE STRENGTH EXCEEDING 1450 MPA |
| BS EN ISO 385:2005 | Laboratory glassware. Burettes |
| DEFSTAN 03-21/5(2011) : 2011 | MECHANICAL METHODS FOR THE INDUCEMENT OF RESIDUAL SURFACE COMPRESSIVE STRESSES |
| BS EN ISO 1042:2000 | Laboratory glassware. One-mark volumetric flasks |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.