SAE AMS4127K
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Aluminum Alloy, Forgings and Rolled or Forged Rings (6061-T6) Solution and Precipitation Heat Treated
Hardcopy , PDF
06-03-2024
English
06-02-2019
Important note : Users cannot be edited or removed once added to your Multi user PDF.This specification covers an aluminum alloy in the form of die forgings not over 4 inches (102 mm) in nominal thickness at time of heat treatment , hand forgings with as-forged thickness not exceeding 8 inches (203 mm) and the cross-sectional area not greater than 256 in2, forged or rolled rings 3.5 inches (89 mm) and under in nominal thickness at time of heat treatment and having an OD-to-wall thickness ratio of 10:1 or greater, and stock of any size for forgings and rings (see 8.6).
| DocumentType |
Standard
|
| Pages |
9
|
| PublisherName |
SAE International
|
| Status |
Superseded
|
| SupersededBy | |
| Supersedes |
This specification covers an aluminum alloy in the form of die forgings not over 4 inches (102 mm) in nominal thickness at time of heat treatment , hand forgings with as-forged thickness not exceeding 8 inches (203 mm) and the cross-sectional area not greater than 256 in2x, forged or rolled rings 3.5 inches (89 mm) and under in nominal thickness at time of heat treatment and having an OD-to-wall thickness ratio of 10:1 or greater, and stock of any size for forgings and rings (see 8.6).
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.