SAEITC TS149-2
Current
The latest, up-to-date edition.
TS149 Technical Specification for All Metal Self-Locking Nuts (UNJ Threads) 1550 MPa (225,000 lbf/in²) Minimum Tensile Strength at Ambient Temperature
Hardcopy , PDF
English
01-12-2004
Important note : Users cannot be edited or removed once added to your Multi user PDF.
1 Foreword
2 Scope
3 Applicable Specifications
4 Definitions
5 Technical Requirements
6 Authorities
7 Qualification Procedure
8 Acceptance of U.S.A. Manufactured Parts
Appendix 1 - Test Fixtures (Including Hardness
Testing)
Appendix 2 - Code Symbols for Manufacturers of Nuts
Appendix 3 - Limitation of Liability
Gives the requirements for all metal self-locking nuts, plate nuts and shank nuts made of heat resisting nickel base alloy which will develop a minimum tensile strength of 1550 MPa (225,000 lbf/in[2]) at ambient temperature.
| DocumentType |
Standard
|
| Pages |
42
|
| PublisherName |
SAE Industry Technologies Consortia
|
| Status |
Current
|
| MIL C 16173 : E | CORROSION PREVENTIVE COMPOUND, SOLVENT CUTBACK, COLD APPLICATION |
| BS 4084:1996 | UNJ threads, with controlled root radius, for aerospace. Inch series |
| MIL L 7808 : K (1) | LUBRICATING OIL, AIRCRAFT TURBINE ENGINE, SYNTHETIC BASE |
| BS M 39:1972 | Method for penetrant inspection of aerospace materials and components |
| SAE AMS 5662 : 2016 | NICKEL ALLOY, CORROSION AND HEAT-RESISTANT, BARS, FORGINGS, AND RINGS 52.5NI - 19CR - 3.0MO - 5.1CB (NB) - 0.90TI - 0.50AI - 18FE CONSUMABLE ELECTRODE OR VACUUM INDUCTION MELTED 1775 DEGREES F (968 DEGREES C) SOLUTION HEAT TREATED, PRECIPITATION-HARDENABLE |
| BS 1134:1961 | Centre-line-average height method for the assessment of surface texture |
| DTD 939 : MAR 66 | SILVER PLATING OF HEAT RESISTANT THREADED PARTS FOR ANTI SEIZURE PURPOSES |
| SAEITC TS48-4 | TS48 Technical Specification for the Performance of Sockets and Ring Spanners |
| MIL-S-8879 Revision C:1991 | SCREW THREADS, CONTROLLED RADIUS ROOT WITH INCREASED MINOR DIAMETER, GENERAL SPECIFICATION FOR |
| SAE AMS 2411 : 2013 | PLATING, SILVER FOR HIGH TEMPERATURE APPLICATIONS |
| DTD 5638 : JUL 85 | HEAT RESISTING NICKEL BASED ALLOY FE-52.5 NI-19 CR-3 MO-5 (N6+TA)-0.9 TI-0.5 AL (VACUUM MELTED) BAR AND WIRE FOR FASTENERS MAXIMUM DIAMETER OR SECTIONAL DIMENSION 50 MM |
| BS 6001(1972) : AMD 5054 | SAMPLING PROCEDURES FOR INSPECTION BY ATTRIBUTES - SPECIFICATION FOR SAMPLING PLANS INDEXED BY ACCEPTABLE QUALITY LEVEL (AQL) FOR LOT - BY - LOT INSPECTION |
| ASTM E 92 : 2017 : REDLINE | Standard Test Methods for Vickers Hardness and Knoop Hardness of Metallic Materials |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.