ASTM B 403 : 2012 : REDLINE

ASTM B 403 : 2012 : REDLINE

Superseded

Superseded

A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.

View Superseded by

Standard Specification for Magnesium-Alloy Investment Castings

Available format(s)

PDF

Superseded date

22-12-2020

Superseded by

ASTM B 403 : 2020 : REDLINE

Language(s)

English

Published date

01-11-2012

Publisher

American Society for Testing and Materials

€59.22
Excluding VAT
EUR
CAD
CHF
CNY
DKK
EUR
GBP
HKD
IDR
INR
JPY
KRW
MXN
NOK
NZD
SEK
SGD
USD
ZAR
PDF - English
01
02
03
04
05
06
07
08
09
10
11
12
13
14
15
16
17
18
19
20

CONTAINED IN VOL. 02.02, 2014 Specifies magnesium-alloy investment castings designated.

Committee
B 07
DocumentType
Redline
Pages
5
PublisherName
American Society for Testing and Materials
Status
Superseded
SupersededBy

1.1This specification covers magnesium-alloy investment castings designated as shown in Table 1.

TABLE 1 Chemical Composition LimitsA
Note 1—Analysis shall regularly be made for the elements specifically mentioned in this table. If, however, the presence of other elements is suspected or indicated in amounts greater than the specified limits, further analysis shall be made to determine that these elements are not present in excess of the specified limits.
Note 2—The following applied to all specified limits in this table: For purposes of acceptance and rejection, an observed value or a calculated value obtained from analysis should be rounded off to the nearest unit in the last right-hand place of figures used in expressing the specified limit.

Alloy Number B

Composition, percent

Others
 Each

 ASTM

 UNS

 Iron

 Magne-
  sium

  Alu-
 minum

 Manga-
  nese

  Zinc

Zirconium

  
 Rare Earths

 Thorium

Copper

 Nickel

Silicon

  TotalC
  Other
Impurities

AM100A

M10100

...

remainder

9.3–10.7

0.10–0.35

0.30

...

...

...

0.10

0.01

0.30

  0.30

  ...

AZ81A

M11810

...

remainder

7.0–8.1

0.13–0.35

0.40–1.0

...

...

...

0.10

0.01

0.30

  0.30

  ...

AZ91C

M11914

...

remainder

8.1–9.3

0.13–0.35

0.40–1.0

...

...

...

0.10

0.01

0.30

  0.30

  ...

AZ91E

M11919

0.005D E

remainder

8.1–9.3

0.17–0.35

0.40–1.0

...

...

...

0.015

0.0010

0.20

  0.30

  0.01

AZ92A

M11920

...

remainder

8.3–9.7

0–0.35

1.6–2.4

...

...

...

0.10

0.01

0.30

  0.30

  ...

EQ21A

M18330

...

remainder

...

...

...

0.40–1.0

1.5–3.0F

...

0.05–0.10

0.01

...

  0.30

  ...

EZ33A

M12330

...

remainder

...

...

2.0–3.1

0.50–1.0

2.5–4.0

...

0.10

0.01

...

  0.30

  ...

K1A

M18010

...

remainder

...

...

...

0.40–1.0

...

...

...

...

...

  0.30

  ...

QE22AG

M18220G

...

remainder

...

...

...

0.40–1.0

1.8–2.5F

...

0.10

0.01

...

  0.30

  ...

ZE41A

M16410

...

remainder

...

0.15

3.5–5.0

0.40–1.0

0.75–1.75

...

0.10

0.01

...

  0.30

  ...

ZK61A

M16610

...

remainder

...

...

5.5–6.5

0.6–1.0

...

...

0.10

0.01

...

  0.30

  ...

A Limits are in weight percent maximum unless shown as a range or stated otherwise.
B  These alloy designations were established in accordance with Practice B951.
C  Includes listed elements for which no specific limit is shown.
D If iron content exceeds 0.005 %, the iron to manganese ratio shall not exceed 0.032.
E Silver content for Alloy EQ21A shall be 1.3 to 1.7 %.
F Rare earth elements are in the form of didymium.
G Silver content for Alloy QE22A shall be 2.0 through 3.0 %.

1.2Alloy designations are in accordance with Practice E527; temper designations are in accordance with Practice B296.

1.3The values stated in inch-pound units are to be regarded as the standard. The SI values in parentheses are for information only.

ASTM B 93/B93M : 2015 : REDLINE Standard Specification for Magnesium Alloys in Ingot Form for Sand Castings, Permanent Mold Castings, and Die Castings
ASTM B 951 : 2011 Standard Practice for Codification of Unalloyed Magnesium and Magnesium-Alloys, Cast and Wrought
ASTM F 3160 : 2016 Standard Guide for Metallurgical Characterization of Absorbable Metallic Materials for Medical Implants
SAE ARP 6256 : 2014 MAGNESIUM ALLOYS IN AIRCRAFT SEATS - ENGINEERING DESIGN AND FABRICATION RECOMMENDED PRACTICES
ASTM B 881 : 2017 : REDLINE Standard Terminology Relating to Aluminum- and Magnesium-Alloy Products

MIL-STD-129 Revision R:2014 Military Marking for Shipment and Storage
ASTM B 666/B666M : 2015 : REDLINE Standard Practice for Identification Marking of Aluminum and Magnesium Products
ASTM E 155 : 2015 : REDLINE Standard Reference Radiographs for Inspection of Aluminum and Magnesium Castings
ASTM B 557 : 2015 : REDLINE Standard Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products
ASTM B 953 : 2013 : REDLINE Standard Practice for Sampling Magnesium and Magnesium Alloys for Spectrochemical Analysis
FED-STD-123 Revision H:2007 MARKING FOR SHIPMENT (CIVIL AGENCIES)
ASTM E 527 : 2016 : REDLINE Standard Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS)
ASTM B 951 : 2011 Standard Practice for Codification of Unalloyed Magnesium and Magnesium-Alloys, Cast and Wrought
ASTM B 661 : 2012 : REDLINE Standard Practice for Heat Treatment of Magnesium Alloys
ASTM B 660 : 2015 : REDLINE Standard Practices for Packaging/Packing of Aluminum and Magnesium Products
ASTM B 954 : 2015 : REDLINE Standard Test Method for Analysis of Magnesium and Magnesium Alloys by Atomic Emission Spectrometry

Access your standards online with a subscription

Features

  • Simple online access to standards, technical information and regulations.

  • Critical updates of standards and customisable alerts and notifications.

  • Multi-user online standards collection: secure, flexible and cost effective.

Get in touch with us