ASTM C 1161 : 2013
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
Hardcopy , PDF
11-11-2014
English
01-08-2013
Committee |
C 28
|
DocumentType |
Test Method
|
Pages |
19
|
PublisherName |
American Society for Testing and Materials
|
Status |
Superseded
|
SupersededBy | |
Supersedes |
1.1This test method covers the determination of flexural strength of advanced ceramic materials at ambient temperature. Four-point–1/4point and three-point loadings with prescribed spans are the standard as shown in Fig. 1. Rectangular specimens of prescribed cross-section sizes are used with specified features in prescribed specimen-fixture combinations. Test specimens may be 3 by 4 by 45 to 50 mm in size that are tested on 40 mm outer span four-point or three-point fixtures. Alternatively, test specimens and fixture spans half or twice these sizes may be used. The method permits testing of machined or as-fired test specimens. Several options for machining preparation are included: application matched machining, customary procedure, or a specified standard procedure. This method describes the apparatus, specimen requirements, test procedure, calculations, and reporting requirements. The test method is applicable to monolithic or particulate- or whisker-reinforced ceramics. It may also be used for glasses. It is not applicable to continuous fiber-reinforced ceramic composites.
1.2The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.3This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
ASTM D 7779 : 2011 : R2015 | Standard Test Method for Determination of Fracture Toughness of Graphite at Ambient Temperature |
ASTM F 603 : 2012 : R2016 | Standard Specification for High-Purity Dense Aluminum Oxide for Medical Application |
ASTM C 1322 : 2015 : R2019 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM F 2393 : 2012 : R2016 | Standard Specification for High-Purity Dense Magnesia Partially Stabilized Zirconia (Mg-PSZ) for Surgical Implant Applications |
ASTM C 1683 : 2010 : R2019 | Standard Practice for Size Scaling of Tensile Strengths Using Weibull Statistics for Advanced Ceramics |
ASTM C 1674 : 2016 | Standard Test Method for Flexural Strength of Advanced Ceramics with Engineered Porosity (Honeycomb Cellular Channels) at Ambient Temperatures |
ASTM C 1495 : 2016 | Standard Test Method for Effect of Surface Grinding on Flexure Strength of Advanced Ceramics |
ASTM C 1576 : 2005 : R2017 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress Flexural Testing (Stress Rupture) at Ambient Temperature |
ASTM D 7972 : 2014 | Standard Test Method for Flexural Strength of Manufactured Carbon and Graphite Articles Using Three-Point Loading at Room Temperature |
ASTM D 7775 : 2016 | Standard Guide for Measurements on Small Graphite Specimens |
ASTM C 1469 : 2010 : R2015 | Standard Test Method for Shear Strength of Joints of Advanced Ceramics at Ambient Temperature |
ASTM C 747 : 2016 | Standard Test Method for Moduli of Elasticity and Fundamental Frequencies of Carbon and Graphite Materials by Sonic Resonance |
ASTM C 1834 : 2016 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress Flexural Testing (Stress Rupture) at Elevated Temperatures |
ASTM C 1273 : 2018 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Ambient Temperatures |
ASTM C 1684 : 2018 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature—Cylindrical Rod Strength |
ASTM C 1211 : 2018 | Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures |
ASTM C 1259 : 2015 | Standard Test Method for Dynamic Young’s Modulus, Shear Modulus, and Poisson’s Ratio for Advanced Ceramics by Impulse Excitation of Vibration |
ASTM C 1421 : 2018 | Standard Test Methods for Determination of Fracture Toughness of Advanced Ceramics at Ambient Temperature |
ASTM C 1366 : 2004 : R2013 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Elevated Temperatures |
ASTM E 1876 : 2015 | Standard Test Method for Dynamic Young's Modulus, Shear Modulus, and Poisson's Ratio by Impulse Excitation of Vibration |
ASTM C 1368 : 2018 | Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress Rate Strength Testing at Ambient Temperature |
ASTM C 651 : 2015 | Standard Test Method for Flexural Strength of Manufactured Carbon and Graphite Articles Using Four-Point Loading at Room Temperature |
ASTM C 1323 : 2016 | Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature |
ASTM C 1198 : 2009 : R2013 | Standard Test Method for Dynamic Young's Modulus, Shear Modulus, and Poisson's Ratio for Advanced Ceramics by Sonic Resonance |
ASTM C 1341 : 2013 : R2018 | Standard Test Method for Flexural Properties of Continuous Fiber-Reinforced Advanced Ceramic Composites |
ASTM F 561 : 2019 | Standard Practice for Retrieval and Analysis of Medical Devices, and Associated Tissues and Fluids |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.