ASTM C 1683 : 2010 : R2015
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Practice for Size Scaling of Tensile Strengths Using Weibull Statistics for Advanced Ceramics
Hardcopy , PDF
12-07-2019
English
01-01-2015
CONTAINED IN VOL. 15.01, 2017 Gives methodology to convert fracture strength parameters estimated from data obtained with one test geometry to strength parameters representing other test geometries.
Committee |
C 28
|
DocumentType |
Standard Practice
|
Pages |
18
|
ProductNote |
Reconfirmed 2015
|
PublisherName |
American Society for Testing and Materials
|
Status |
Superseded
|
SupersededBy |
1.1This standard practice provides methodology to convert fracture strength parameters (primarily the mean strength and the Weibull characteristic strength) estimated from data obtained with one test geometry to strength parameters representing other test geometries. This practice addresses uniaxial strength data as well as some biaxial strength data. It may also be used for more complex geometries proved that the effective areas and effective volumes can be estimated. It is for the evaluation of Weibull probability distribution parameters for advanced ceramics that fail in a brittle fashion. Fig. 1 shows the typical variation of strength with size. The larger the specimen or component, the weaker it is likely to be.
Annex A3
1.5The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.5.1The values stated in SI units are in accordance with IEEE/ASTM SI 10.
1.6This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
ASTM C 1783 : 2015 | Standard Guide for Development of Specifications for Fiber Reinforced Carbon-Carbon Composite Structures for Nuclear Applications |
ASTM C 1323 : 2016 | Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature |
ASTM C 1793 : 2015 | Standard Guide for Development of Specifications for Fiber Reinforced Silicon Carbide-Silicon Carbide Composite Structures for Nuclear Applications |
ASTM C 1323 : 2016 : REDLINE | Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature |
ASTM C 1322 : 2015 : REDLINE | PRACTICE FOR FRACTOGRAPHY AND CHARACTERIZATION OF FRACTURE ORIGINS IN ADVANCED CERAMICS |
ASTM C 1499 : 2015 : REDLINE | TEST METHOD FOR MONOTONIC EQUIBIAXIAL FLEXURAL STRENGTH OF ADVANCED CERAMICS AT AMBIENT TEMPERATURE |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.