Standard Practice for Size Scaling of Tensile Strengths Using Weibull Statistics for Advanced Ceramics
Hardcopy , PDF
07-10-2024
English
01-07-2019
This standard practice provides methodology to convert fracture strength parameters (primarily the mean strength and the Weibull characteristic strength) estimated from data obtained with one test geometry to strength parameters representing other test geometries.
Committee |
C 28
|
DocumentType |
Standard Practice
|
Pages |
18
|
PublisherName |
American Society for Testing and Materials
|
Status |
Superseded
|
SupersededBy | |
Supersedes |
1.1This standard practice provides methodology to convert fracture strength parameters (primarily the mean strength and the Weibull characteristic strength) estimated from data obtained with one test geometry to strength parameters representing other test geometries. This practice addresses uniaxial strength data as well as some biaxial strength data. It may also be used for more complex geometries proved that the effective areas and effective volumes can be estimated. It is for the evaluation of Weibull probability distribution parameters for advanced ceramics that fail in a brittle fashion. Fig. 1 shows the typical variation of strength with size. The larger the specimen or component, the weaker it is likely to be.
1.5The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.5.1The values stated in SI units are in accordance with IEEE/ASTM SI 10.
1.6This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.7This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM C 1793 : 2015 | Standard Guide for Development of Specifications for Fiber Reinforced Silicon Carbide-Silicon Carbide Composite Structures for Nuclear Applications |
ASTM C 1783 : 2015 | Standard Guide for Development of Specifications for Fiber Reinforced Carbon-Carbon Composite Structures for Nuclear Applications |
ASTM C 1323 : 2016 | Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature |
ASTM C 1899 : 2021 | Standard Test Method for Flexural Strength of Continuous Fiber-Reinforced Advanced Ceramic Tubular Test Specimens at Ambient Temperature |
ASTM C 1783 : 2015 : R2024 | Standard Guide for Development of Specifications for Fiber Reinforced Carbon-Carbon Composite Structures for Nuclear Applications |
ASTM C 1793 : 2015 : R2024 | Standard Guide for Development of Specifications for Fiber Reinforced Silicon Carbide-Silicon Carbide Composite Structures for Nuclear Applications |
ASTM C 1499 : 2015 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1145 : 2019 | Standard Terminology of Advanced Ceramics |
ASTM C 1211 : 2018 | Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures |
ASTM C 1211 : 2013 | Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures |
ASTM C 1322 : 2005 : REV B | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM C 1145 : 1998 | Standard Terminology of Advanced Ceramics |
ASTM C 1161 : 2002 : REV C : R2008 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1145 : 2006 | Standard Terminology of Advanced Ceramics |
ASTM E 456 : 2002 | Standard Terminology for Relating to Quality and Statistics |
ASTM C 1161 : 2002 : REV C : R2008 : EDT 1 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM E 456 : 2013 : REV A : R2022 | Standard Terminology Relating to Quality and Statistics |
ASTM C 1499 : 2004 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1273 : 2018 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Ambient Temperatures |
ASTM C 1161 : 2018 : R2023 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM E 456 : 2013 : REV A : R2022 : EDT 1 | Standard Terminology Relating to Quality and Statistics |
ASTM C 1322 : 2015 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM C 1322 : 2005 : REV A | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM C 1499 : 2003 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1499 : 2005 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1145 : 2005 | Standard Terminology of Advanced Ceramics |
ASTM C 1161 : 2002 : REV C : EDT 1 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1499 : 2009 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1273 : 1995 : REV A : R2000 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Ambient Temperatures |
ASTM E 6 : 2002 | Standard Terminology Relating to Methods of Mechanical Testing |
ASTM C 1323 : 2016 | Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature |
ASTM C 1366 : 1997 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Elevated Temperatures |
ASTM C 1322 : 2005 : REV B : EDT 1 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM E 456 : 2013 : REV A : R2017 : EDT 5 | Standard Terminology Relating to Quality and Statistics |
ASTM C 1161 : 2002 : REV A | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1239 : 2006 : REV A | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM C 1366 : 2019 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Elevated Temperatures |
ASTM C 1145 : 2003 | Standard Terminology of Advanced Ceramics |
ASTM C 1323 : 2010 | Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature |
ASTM C 1273 : 2015 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Ambient Temperatures |
ASTM C 1499 : 2008 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1499 : 2019 : R2024 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1322 : 2015 : R2024 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM C 1239 : 2013 : R2018 | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM E 456 : 2013 | Standard Terminology Relating to Quality and Statistics |
ASTM C 1322 : 2005 : REV B : R2010 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM C 1322 : 1996 : REV A | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM C 1161 : 2018 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1211 : 1998 : REV A | Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures |
ASTM C 1323 : 1996 | Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature |
ASTM C 1161 : 2002 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1322 : 2002 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM C 1499 : 2002 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM E 6 : 2015 : EDT 3 | Standard Terminology Relating to Methods of Mechanical Testing |
ASTM C 1366 : 2004 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Elevated Temperatures |
ASTM C 1499 : 2001 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1239 : 2000 | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM E 6 : 2023 : REV A | Standard Terminology Relating to Methods of Mechanical Testing |
ASTM C 1145 : 2006 : R2013 | Standard Terminology of Advanced Ceramics |
ASTM C 1161 : 2013 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1239 : 2000 : R2005 | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM C 1323 : 1996 : R2001 | Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature |
ASTM C 1322 : 2002 : REV A | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM C 1499 : 2009 : R2013 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1145 : 2002 | Standard Terminology of Advanced Ceramics |
ASTM C 1323 : 1996 : R2001 : EDT 1 | Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature |
ASTM C 1211 : 2018 : R2023 | Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures |
ASTM C 1366 : 2004 : R2013 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Elevated Temperatures |
ASTM C 1322 : 2015 : R2019 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM E 6 : 2015 : EDT 4 : REDLINE | Standard Terminology Relating to Methods of Mechanical Testing |
ASTM C 1211 : 2002 | Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures |
ASTM C 1273 : 2005 : R2010 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Ambient Temperatures |
ASTM C 1161 : 1994 : R1996 | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1239 : 2006 | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM C 1273 : 2018 : R2024 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Ambient Temperatures |
ASTM C 1366 : 2004 : R2009 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Elevated Temperatures |
ASTM C 1145 : 2002 : REV A | Standard Terminology of Advanced Ceramics |
ASTM C 1161 : 2002 : REV C | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1499 : 2019 | Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature |
ASTM C 1322 : 2005 | Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics |
ASTM E 6 : 2015 : EDT 4 | Standard Terminology Relating to Methods of Mechanical Testing |
ASTM E 6 : 2023 | Standard Terminology Relating to Methods of Mechanical Testing |
ASTM E 456 : 2013 : REV A : R2017 : EDT 4 | Standard Terminology Relating to Quality and Statistics |
ASTM E 456 : 2013 : REV A : R2017 : EDT 6 | Standard Terminology Relating to Quality and Statistics |
ASTM C 1145 : 2001 | Standard Terminology of Advanced Ceramics |
ASTM C 1239 : 2013 | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM C 1239 : 2007 | Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics |
ASTM C 1323 : 2022 | Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature |
ASTM C 1145 : 2006 : R2013 : EDT 1 | Standard Terminology of Advanced Ceramics |
ASTM C 1211 : 2002 : R2008 | Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures |
ASTM C 1273 : 2005 | Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Ambient Temperatures |
ASTM C 1161 : 2002 : REV B | Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.