ASTM C 505 : 2019
Current
The latest, up-to-date edition.
Standard Specification for Nonreinforced Concrete Irrigation Pipe with Rubber Gasket Joints
Hardcopy , PDF
English
01-07-2019
Important note : Users cannot be edited or removed once added to your Multi user PDF.
This specification covers nonreinforced concrete pipe with rubber gasket joints to be used for the conveyance of irrigation water with working pressures, including hydraulic transients, as shown in Table 1.
| Committee |
C 13
|
| DocumentType |
Standard
|
| Pages |
5
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Current
|
| Supersedes |
1.1 This specification covers nonreinforced concrete pipe with rubber gasket joints to be used for the conveyance of irrigation water with working pressures, including hydraulic transients, as shown in Table 1.
1.2A complete metric companion to Specification C505 has been developed—C505M; therefore, no SI equivalents are presented in this specification.
Note 1:This specification is for manufacturing and purchase only and does not include requirements for bedding, backfill, installation, or field repairs. The owner is cautioned that he must correlate field conditions with the characteristics of the pipe specified and provide inspection during installation.
1.3This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
| ASTM D 2240 : 2000 | Standard Test Method for Rubber Property—Durometer Hardness |
| ASTM D 471 : 2016 : REV A | Standard Test Method for Rubber Property—Effect of Liquids |
| ASTM C 150/C150M : 2024 | Standard Specification for Portland Cement |
| ASTM C 822 : 2021 | Standard Terminology Relating to Concrete Pipe and Related Products |
| ASTM D 1149 : 2016 | Standard Test Methods for Rubber Deterioration—Cracking in an Ozone Controlled Environment |
| ASTM C 33/C33M : 2023 | Standard Specification for Concrete Aggregates |
| ASTM C 494/C494M : 2019 | Standard Specification for Chemical Admixtures for Concrete |
| ASTM C 494/C494M : 2019 : EDT 1 | Standard Specification for Chemical Admixtures for Concrete |
| ASTM D 1415 : 2005 | Standard Test Method for Rubber Property—International Hardness |
| ASTM C 33/C33M : 2018 | Standard Specification for Concrete Aggregates |
| ASTM C 1116/C1116M : 2010 : REV A : R2015 | Standard Specification for Fiber-Reinforced Concrete |
| ASTM D 1415 : 1988 : R1999 | Standard Test Method for Rubber Property-International Hardness |
| ASTM C 595/C595M : 2021 | Standard Specification for Blended Hydraulic Cements |
| ASTM D 1415 : 2018 | Standard Test Method for Rubber Property—International Hardness |
| ASTM D 1415 : 1988 : R2004 | Standard Test Method for Rubber Property—International Hardness |
| ASTM D 2240 : 2004 | Standard Test Method for Rubber Property—Durometer Hardness |
| ASTM C 989/C989M : 2018 : REV A | Standard Specification for Slag Cement for Use in Concrete and Mortars |
| ASTM D 1149 : 2015 | Standard Test Methods for Rubber Deterioration—Cracking in an Ozone Controlled Environment |
| ASTM D 412 : 2016 : EDT 1 | Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers—Tension |
| ASTM C 595/C595M : 2020 | Standard Specification for Blended Hydraulic Cements |
| ASTM C 33/C33M : 2024 | Standard Specification for Concrete Aggregates |
| ASTM D 1149 : 2007 | Standard Test Methods for Rubber Deterioration-Cracking in an Ozone Controlled Environment |
| ASTM C 822 : 2020 | Standard Terminology Relating to Concrete Pipe and Related Products |
| ASTM C 618 : 2023 : EDT 1 | Standard Specification for Coal Ash and Raw or Calcined Natural Pozzolan for Use in Concrete |
| ASTM D 2240 : 2004 : EDT 1 | Standard Test Method for Rubber Property—Durometer Hardness |
| ASTM D 471 : 2016 : REV A : R2021 | Standard Test Method for Rubber Property—Effect of Liquids |
| ASTM C 1017/C1017M : 2013 : EDT 1 | Standard Specification for Chemical Admixtures for Use in Producing Flowing Concrete (Withdrawn 2022) |
| ASTM C 150/C150M : 2021 | Standard Specification for Portland Cement |
| ASTM D 412 : 2016 | Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers—Tension |
| ASTM C 33/C33M : 2024 : REV A | Standard Specification for Concrete Aggregates |
| ASTM C 618 : 2022 | Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete |
| ASTM D 1149 : 2018 | Standard Test Methods for Rubber Deterioration—Cracking in an Ozone Controlled Environment |
| ASTM D 1415 : 1968 | Standard Test Method for International Hardness Of Vulcanized Rubber |
| ASTM D 2240 : 2015 : R2021 | Standard Test Method for Rubber Property—Durometer Hardness |
| ASTM C 1602/C1602M : 2018 | Standard Specification for Mixing Water Used in the Production of Hydraulic Cement Concrete |
| ASTM D 2240 : 2002 | Standard Test Method for Rubber Property—Durometer Hardness |
| ASTM C 618 : 2023 | Standard Specification for Coal Ash and Raw or Calcined Natural Pozzolan for Use in Concrete |
| ASTM D 2240 : 2015 | Standard Test Method for Rubber Property—Durometer Hardness |
| ASTM D 1149 : 2007 : R2012 | Standard Test Methods for Rubber Deterioration—Cracking in an Ozone Controlled Environment |
| ASTM D 2240 : 2003 | Standard Test Method for Rubber Property—Durometer Hardness |
| ASTM C 1602/C1602M : 2022 | Standard Specification for Mixing Water Used in the Production of Hydraulic Cement Concrete |
| ASTM D 1149 : 1978 : REV A | Standard Test Method for Rubber Deterioration - Surface Ozone Cracking In A Chamber ( Flat Specimen) |
| ASTM C 595/C595M : 2024 | Standard Specification for Blended Hydraulic Cements |
| ASTM D 2240 : 2002 : REV B | Standard Test Method for Rubber Property—Durometer Hardness |
| ASTM C 595/C595M : 2023 | Standard Specification for Blended Hydraulic Cements |
| ASTM D 1415 : 2006 : R2012 | Standard Test Method for Rubber Property—International Hardness |
| ASTM D 1415 : 2006 | Standard Test Method for Rubber Property—International Hardness |
| ASTM C 494/C494M : 2010 | Standard Specification for Chemical Admixtures for Concrete |
| ASTM D 2240 : 2015 : EDT 1 | Standard Test Method for Rubber Property—Durometer Hardness |
| ASTM C 989/C989M : 2024 | Standard Specification for Slag Cement for Use in Concrete and Mortars |
| ASTM D 412 : 2016 : R2021 | Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers—Tension |
| ASTM C 1116/C1116M : 2023 | Standard Specification for Fiber-Reinforced Concrete |
| ASTM C 618 : 2019 | Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete |
| ASTM D 2240 : 2005 | Standard Test Method for Rubber Property—Durometer Hardness |
| ASTM C 494/C494M : 2024 | Standard Specification for Chemical Admixtures for Concrete |
| ASTM C 150/C150M : 2020 | Standard Specification for Portland Cement |
| ASTM D 2240 : 2005 : R2010 | Standard Test Method for Rubber Property—Durometer Hardness |
| ASTM C 989/C989M : 2022 | Standard Specification for Slag Cement for Use in Concrete and Mortars |
| ASTM C 497 : 1998 | Standard Test Methods for Concrete Pipe, Manhole Sections, or Tile |
| ASTM C 150/C150M : 2022 | Standard Specification for Portland Cement |
| ASTM D 2240 : 2002 : REV A | Standard Test Method for Rubber Property—Durometer Hardness |
| ASTM D 1149 : 1999 | Standard Test Method for Rubber Deterioration-Surface Ozone Cracking in a Chamber |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.