ASTM C 838 : 2016 : REDLINE
Current
The latest, up-to-date edition.
Standard Test Method for Bulk Density of As-Manufactured Carbon and Graphite Shapes
English
05-02-2016
Important note : Users cannot be edited or removed once added to your Multi user PDF.CONTAINED IN VOL. 05.05, 2017 Defines the determination of the density of as-manufactured carbon and graphite from measurements of mass and dimensions at room temperature.
| Committee |
D 02
|
| DocumentType |
Redline
|
| Pages |
2
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Current
|
1.1This test method covers the determination of the density of as-manufactured carbon and graphite from measurements of mass and dimensions at room temperature.
1.2This test method is applicable to boronated carbon and graphite.
1.3This test method is not applicable to carbon- and graphite-containing materials that are thermally unstable at or below temperatures of 200 °C.
1.4The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.5This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
| MIL-PRF-32577 Base Document:2017 | Coating System, Nonskid, Metallic Thermal Spray Application |
| ASTM C 1039 : 1985 : R2005 | Standard Test Methods for Apparent Porosity, Apparent Specific Gravity, and Bulk Density of Graphite Electrodes |
| ASTM D 7301 : 2011 : R2015 | Standard Specification for Nuclear Graphite Suitable for Components Subjected to Low Neutron Irradiation Dose |
| ASTM C 1039 : 1985 : R2000 | Standard Test Methods for Apparent Porosity, Apparent Specific Gravity, and Bulk Density of Graphite Electrodes |
| ASTM C 1836 : 2016 | Standard Classification for Fiber Reinforced Carbon-Carbon Composite Structures |
| ASTM D 7219 : 2008 : R2014 | Standard Specification for Isotropic and Near-isotropic Nuclear Graphites |
| ASTM C 781 : 2008 | Standard Practice for Testing Graphite and Boronated Graphite Materials for High-Temperature Gas-Cooled Nuclear Reactor Components |
| ASTM C 1783 : 2015 | Standard Guide for Development of Specifications for Fiber Reinforced Carbon-Carbon Composite Structures for Nuclear Applications |
| ASTM C 1793 : 2015 | Standard Guide for Development of Specifications for Fiber Reinforced Silicon Carbide-Silicon Carbide Composite Structures for Nuclear Applications |
| ASTM C 781 : 2008 : R2014 | Standard Practice for Testing Graphite and Boronated Graphite Materials for High-Temperature Gas-Cooled Nuclear Reactor Components |
| ASTM C 1039 : 1985 : R2015 | Standard Test Methods for Apparent Porosity, Apparent Specific Gravity, and Bulk Density of Graphite Electrodes |
| ASTM C 1039 : 1985 : R2010 : EDT 1 | Standard Test Methods for Apparent Porosity, Apparent Specific Gravity, and Bulk Density of Graphite Electrodes |
| ASTM D 7301 : 2011 | Standard Specification for Nuclear Graphite Suitable for Components Subjected to Low Neutron Irradiation Dose |
| ASTM D 7219 : 2008 | Standard Specification for Isotropic and Near-isotropic Nuclear Graphites |
| ASTM C 559 : 2016 : REDLINE | Standard Test Method for Bulk Density by Physical Measurements of Manufactured Carbon and Graphite Articles |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.