1.1These test methods are designed to characterize the toughness of plastics in terms of the critical-stress-intensity factor, KIc, and the energy per unit area of crack surface or critical strain energy release rate, GIc, at fracture initiation.
1.2Two testing geometries are covered by these test methods, single-edge-notch bending (SENB) and compact tension (CT).
1.3The scheme used assumes linear elastic behavior of the cracked specimen, so certain restrictions on linearity of the load-displacement diagram are imposed.
1.4A state-of-plane strain at the crack tip is required. Specimen thickness must be sufficient to ensure this stress state.
1.5The crack must be sufficiently sharp to ensure that a minimum value of toughness is obtained.
1.6The significance of these test methods and many conditions of testing are identical to those of Test Method E399, and, therefore, in most cases, appear here with many similarities to the metals standard. However, certain conditions and specifications not covered in Test Method E399, but important for plastics, are included.
1.7This protocol covers the determination of GIc as well, which is of particular importance for plastics.
1.8These test methods give general information concerning the requirements for KIc and GIc testing. As with Test Method E399, two annexes are provided which give the specific requirements for testing of the SENB and CT geometries.
1.9Test data obtained by these test methods are relevant and appropriate for use in engineering design.
1.10This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Note 1:This standard and ISO 13586 address the same subject matter, but differ in technical content.