ASTM E 1434 : 2000 : R2006
Withdrawn
A Withdrawn Standard is one, which is removed from sale, and its unique number can no longer be used. The Standard can be withdrawn and not replaced, or it can be withdrawn and replaced by a Standard with a different number.
View Superseded by
Standard Guide for Recording Mechanical Test Data of Fiber-Reinforced Composite Materials in Databases
Hardcopy , PDF
01-08-2015
English
15-01-2006
CONTAINED IN VOL. 15.03, 2014 Gives a common format for mechanical test data for composite materials for two purposes: 1) To establish data reporting requirements for test methods; and 2) To provide information for the design of material property databases.
Committee |
D 30
|
DocumentType |
Guide
|
Pages |
17
|
ProductNote |
Reconfirmed 2006
|
PublisherName |
American Society for Testing and Materials
|
Status |
Withdrawn
|
SupersededBy | |
Supersedes |
1.1 This guide provides a common format for mechanical test data for composite materials for two purposes: (1) to establish data reporting requirements for test methods and ( 2) to provide information for the design of material property databases. This guide should be used in combination with Guide E 1309 which provides similar information to identify the composite material tested.
1.2 These guidelines are specific to mechanical tests of high-modulus fiber-reinforced composite materials. Types of tests considered in this guide include tension, compression, shear, flexure, open/filled hole, bearing, fracture toughness, and fatigue. The ASTM standards for which this guide was developed are listed in . The guidelines may also be useful for additional tests or materials.
1.3 This guide is the second part of a modular approach for which the first part is Guide E 1309. Guide E 1309 serves to identify the material, and this guide serves to describe mechanical testing procedures and variables and to record results. The interaction of this guide with Guide E 1309 is emphasized by the common numbering of data elements. Data Elements A1 through G13 are included in Guide E 1309 and numbering data elements in this guide begins with H1.
1.4 This guide with Guide E 1309 may be referenced by the data-reporting section of a test method to provide common data-reporting requirements for the types of tests listed in .
1.5 From this information and Guide E 1309, the database designer should be able to construct the data dictionary preparatory to developing a database schema.
1.6 Data elements in this guide are relevant to test data, data as obtained in the test laboratory and historically recorded in lab notebooks. Property data, data which have been analyzed and reviewed, require a different level of data elements. Data elements for property data are provided in .
ASTM D 7905/D7905M : 2019 | Standard Test Method for Determination of the Mode II Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix Composites |
ASTM D 8069 : 2017 : REV A | Standard Test Method for Determining Flexural Modulus of Full Section Pultruded Fiber Reinforced Polymer (FRP) Composite Members with Doubly Symmetric Cross Sections under Bending |
ASTM D 2344/D2344M : 2016 | Standard Test Method for Short-Beam Strength of Polymer Matrix Composite Materials and Their Laminates |
ASTM D 5961/D5961M : 2017 | Standard Test Method for Bearing Response of Polymer Matrix Composite Laminates |
ASTM D 5528 : 2013 | Standard Test Method for Mode I Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix Composites |
ASTM E 2581 : 2014 | Standard Practice for Shearography of Polymer Matrix Composites and Sandwich Core Materials in Aerospace Applications |
ASTM D 7205/D7205M : 2006 : R2016 | Standard Test Method for Tensile Properties of Fiber Reinforced Polymer Matrix Composite Bars |
ASTM D 7264/D7264M : 2015 | Standard Test Method for Flexural Properties of Polymer Matrix Composite Materials |
ASTM D 7028 : 2007 : R2015 | Standard Test Method for Glass Transition Temperature (DMA Tg) of Polymer Matrix Composites by Dynamic Mechanical Analysis (DMA) |
ASTM D 4255/D4255M : 2015 : REV A | Standard Test Method for In-Plane Shear Properties of Polymer Matrix Composite Materials by the Rail Shear Method |
ASTM D 7078/D7078M : 2012 | Standard Test Method for Shear Properties of Composite Materials by V-Notched Rail Shear Method |
ASTM E 2580 : 2017 | Standard Practice for Ultrasonic Testing of Flat Panel Composites and Sandwich Core Materials Used in Aerospace Applications |
ASTM D 5467/D5467M : 1997 : R2017 | Standard Test Method for Compressive Properties of Unidirectional Polymer Matrix Composite Materials Using a Sandwich Beam |
ASTM D 7291/D7291M : 2015 | Standard Test Method for Through-Thickness “Flatwise” Tensile Strength and Elastic Modulus of a Fiber-Reinforced Polymer Matrix Composite Material |
ASTM D 7332/D7332M : 2016 | Standard Test Method for Measuring the Fastener Pull-Through Resistance of a <brk/>Fiber-Reinforced Polymer Matrix Composite |
ASTM D 6415/D6415M : 2006 : REV A : R2013 | Standard Test Method for Measuring the Curved Beam Strength of a Fiber-Reinforced Polymer-Matrix Composite |
ASTM D 6641/D6641M : 2016 : EDT 1 | Standard Test Method for Compressive Properties of Polymer Matrix Composite Materials Using a Combined Loading Compression (CLC) Test Fixture |
ASTM D 7136/D7136M : 2015 | Standard Test Method for Measuring the Damage Resistance of a Fiber-Reinforced Polymer Matrix Composite to a Drop-Weight Impact Event |
ASTM D 7248/D7248M : 2012 : R2017 | Standard Test Method for Bearing/Bypass Interaction Response of Polymer Matrix Composite Laminates Using 2-Fastener Specimens |
ASTM D 5687/D5687M : 1995 : R2015 | Standard Guide for Preparation of Flat Composite Panels with Processing Guidelines for Specimen Preparation |
ASTM D 3410/D3410M : 2016 | Standard Test Method for Compressive Properties of Polymer Matrix Composite Materials with Unsupported Gage Section by Shear Loading |
ASTM D 6484/D6484M : 2014 | Standard Test Method for Open-Hole Compressive Strength of Polymer Matrix Composite Laminates |
ASTM D 5961/D5961M : 2017 : REDLINE | Standard Test Method for Bearing Response of Polymer Matrix Composite Laminates |
ASTM D 5449/D5449M : 2016 : REDLINE | Standard Test Method for Transverse Compressive Properties of Hoop Wound Polymer Matrix Composite Cylinders |
ASTM D 5229/D5229M : 2014-06 | TEST METHOD FOR MOISTURE ABSORPTION PROPERTIES AND EQUILIBRIUM CONDITIONING OF POLYMER MATRIX COMPOSITE MATERIALS |
ASTM D 5528 : 2013 : REDLINE | Standard Test Method for Mode I Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix Composites |
ASTM D 5379/D5379M : 2012 : REDLINE | Standard Test Method for Shear Properties of Composite Materials by the V-Notched Beam Method |
ASTM D 3410/D3410M : 2016 : REDLINE | Standard Test Method for Compressive Properties of Polymer Matrix Composite Materials with Unsupported Gage Section by Shear Loading |
IEEE/ASTM SI_10-2010 | American National Standard for Metric Practice |
ASTM D 3518/D3518M : 2013-09 | TEST METHOD FOR IN-PLANE SHEAR RESPONSE OF POLYMER MATRIX COMPOSITE MATERIALS BY TENSILE TEST OF A +/-45 DEGREES LAMINATE |
ISO 8601:2004 | Data elements and interchange formats Information interchange Representation of dates and times |
ASTM D 790 : 2017 : REDLINE | Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials |
ASTM D 3552 : 2017 : REDLINE | Standard Test Method for Tensile Properties of Fiber Reinforced Metal Matrix Composites |
ASTM E 111 : 2017 : REDLINE | Standard Test Method for Young’s Modulus, Tangent Modulus, and Chord Modulus |
ASTM D 3039/D3039M : 2017 : REDLINE | Standard Test Method for Tensile Properties of Polymer Matrix Composite Materials |
ASTM E 1484 : 1992 | GUIDE FOR FORMATTING AND USE OF MATERIAL AND CHEMICAL PROPERTY DATA AND DATABASE QUALITY INDICATORS |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.