TEST METHOD FOR MEASUREMENT OF HYDROGEN EMBRITTLEMENT THRESHOLD IN STEEL BY THE INCREMENTAL STEP LOADING TECHNIQUE
Published date
01-11-2012
CONTAINED IN VOL. 15.03, 2015 Defines a procedure to measure the susceptibility of steel to a time-delayed failure such as that caused by hydrogen.
Committee |
F 07
|
DocumentType |
Redline
|
PublisherName |
American Society for Testing and Materials
|
Status |
NA
|
ASTM F 2078 : 2015 : REDLINE | Standard Terminology Relating to Hydrogen Embrittlement Testing |
BS ISO 16110-1:2007 | Hydrogen generators using fuel processing technologies Safety |
DIN EN ISO 7539-11:2015-03 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION CRACKING - PART 11: GUIDELINES FOR TESTING THE RESISTANCE OF METALS AND ALLOYS TO HYDROGEN EMBRITTLEMENT AND HYDROGEN-ASSISTED CRACKING (ISO 7539-11:2013) |
IFI 144 : 2000 : R2013 | TEST EVALUATION PROCEDURES FOR COATING QUALIFICATION INTENDED FOR USE ON HIGH-STRENGTH STRUCTURAL BOLTS |
ASTM F 2833 : 2011 | Standard Specification for Corrosion Protective Fastener Coatings with Zinc Rich Base Coat and Aluminum Organic/Inorganic Type |
ASTM F 2660 : 2013 : REDLINE | Standard Test Method for Qualifying Coatings for Use on A490 Structural Bolts Relative to Environmental Hydrogen Embrittlement |
ISO 7539-11:2013 | Corrosion of metals and alloys — Stress corrosion testing — Part 11: Guidelines for testing the resistance of metals and alloys to hydrogen embrittlement and hydrogen-assisted cracking |
DIN EN ISO 7539-11 E : 2015 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION CRACKING - PART 11: GUIDELINES FOR TESTING THE RESISTANCE OF METALS AND ALLOYS TO HYDROGEN EMBRITTLEMENT AND HYDROGEN-ASSISTED CRACKING (ISO 7539-11:2013) |
BS ISO 7539-11 : 2013 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION CRACKING - PART 11: GUIDELINES FOR TESTING THE RESISTANCE OF METALS AND ALLOYS TO HYDROGEN EMBRITTLEMENT AND HYDROGEN-ASSISTED CRACKING |
BS ISO 16111:2008 | Transportable gas storage devices. Hydrogen absorbed in reversible metal hydride |
ASTM F 1940 : 2007 : REV A : R2014 | Standard Test Method for Process Control Verification to Prevent Hydrogen Embrittlement in Plated or Coated Fasteners |
ISO 16110-1:2007 | Hydrogen generators using fuel processing technologies Part 1: Safety |
ASTM F 1941/F1941M : 2016 : REDLINE | Standard Specification for Electrodeposited Coatings on Mechanical Fasteners, Inch and Metric |
UNE-EN ISO 7539-11:2015 | Corrosion of metals and alloys - Stress corrosion cracking - Part 11: Guidelines for testing the resistance of metals and alloys to hydrogen embrittlement and hydrogen-assisted cracking (ISO 7539-11:2013) |
17/30341479 DC : 0 | BS ISO 16111 - TRANSPORTABLE GAS STORAGE DEVICES - HYDROGEN ABSORBED IN REVERSIBLE METAL HYDRIDE |
IFI 144 : 2000 | TEST EVALUATION PROCEDURES FOR COATING QUALIFICATION INTENDED FOR USE ON HIGH-STRENGTH STRUCTURAL BOLTS |
ASTM F 1940 : 2007 | Standard Test Method for Process Control Verification to Prevent Hydrogen Embrittlement in Plated or Coated Fasteners |
ASTM F 3019/F3019M : 2014 | Standard Specification for Chromium Free Zinc-Flake Composite, with or without Integral Lubricant, Corrosion Protective Coatings for Fasteners |
ASTM F 1940 : 2007 : REV A | Standard Test Method for Process Control Verification to Prevent Hydrogen Embrittlement in Plated or Coated Fasteners |
ISO 16111:2008 | Transportable gas storage devices Hydrogen absorbed in reversible metal hydride |
ASTM F 606/F606M : 2016 : REDLINE | Standard Test Methods for Determining the Mechanical Properties of Externally and Internally Threaded Fasteners, Washers, Direct Tension Indicators, and Rivets |
11/30219194 DC : 0 | BS ISO 7539-11 - CORROSION OF METALS AND ALLOYS - STRESS CORROSION CRACKING - PART 11: GUIDELINES FOR TESTING THE RESISTANCE OF METALS AND ALLOYS TO HYDROGEN EMBRITTLEMENT AND HYDROGEN-ASSISTED CRACKING |
ANSI/CSA FC 1:2014 | FUEL CELL TECHNOLOGIES - PART 3-100: STATIONARY FUEL CELL POWER SYSTEMS - SAFETY |
I.S. EN ISO 7539-11:2014 | CORROSION OF METALS AND ALLOYS - STRESS CORROSION CRACKING - PART 11: GUIDELINES FOR TESTING THE RESISTANCE OF METALS AND ALLOYS TO HYDROGEN EMBRITTLEMENT AND HYDROGEN-ASSISTED CRACKING (ISO 7539-11:2013) |
UNE-ISO 16110-1:2015 | Hydrogen generators using fuel processing technologies -- Part 1: Safety |
EN ISO 7539-11:2014 | Corrosion of metals and alloys - Stress corrosion testing - Part 11: Guidelines for testing the resistance of metals and alloys to hydrogen embrittlement and hydrogen-assisted cracking (ISO 7539-11:2013) |
BS EN ISO 7539-11:2014 | Corrosion of metals and alloys. Stress corrosion cracking Guidelines for testing the resistance of metals and alloys to hydrogen embrittlement and hydrogen-assisted cracking |
SAE J 2579 : 2013 | STANDARD FOR FUEL SYSTEMS IN FUEL CELL AND OTHER HYDROGEN VEHICLES |
ASTM F 2833 : 2011 : R2017 | Standard Specification for Corrosion Protective Fastener Coatings with Zinc Rich Base Coat and Aluminum Organic/Inorganic Type |
SAE J 78 : 2013 | STEEL SELF-DRILLING TAPPING SCREWS |
ASTM E 812 : 1991 : R1997 | Standard Test Method for Crack Strength of Slow-Bend Precracked Charpy Specimens of High-Strength Metallic Materials (Withdrawn 2005) |
SAE J 81 : 2012 | THREAD ROLLING SCREWS |
ASTM F 2078 : 2015 : REDLINE | Standard Terminology Relating to Hydrogen Embrittlement Testing |
ASTM A 574 : 2017 : REDLINE | Standard Specification for Alloy Steel Socket-Head Cap Screws |
SAE J 1237 : 2001 | METRIC THREAD ROLLING SCREWS |
ASTM E 8/E8M : 2016-09 | TEST METHODS FOR TENSION TESTING OF METALLIC MATERIALS |
Sorry this product is not available in your region.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.