1.1This test method describes the collection of absorption spectra of polyetheretherketone (PEEK) polymer in filled and unfilled grades, as supplied by a vendor, and the subsequent calculation of the percent crystallinity. The material is evaluated by infrared spectroscopy. The intensity (height) of the absorbance peaks is related to the amount of crystalline regions present in the material.

1.2This test method can be used for PEEK consolidated forms, such as injection molded parts, as long as the samples are optically flat and smooth.

1.3The applicability of the infrared method to industrial and medical grade PEEK materials has been demonstrated by scientific studies.2, 3 Percentage of crystallinity is related to R-FTIR measurement by calibration through wide-angle x-ray scattering (WAXS) crystallinity measurements.2, 3 It is anticipated that this test method, involving the peak heights near 1305 cm^-1 and 1280 cm^-1, will be evaluated in an Interlaboratory Study (ILS) conducted according to Test Method E691.

1.4This test method does not suggest a desired range of crystallinity for specific applications.

1.5The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.

1.6This standard may involve hazardous materials, operations, and equipment. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.7This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.