ASTM G 38 : 2001 : R2021
Current
The latest, up-to-date edition.
Standard Practice for Making and Using C-Ring Stress-Corrosion Test Specimens
Hardcopy , PDF
English
04-08-2021
Important note : Users cannot be edited or removed once added to your Multi user PDF.| Committee |
G 01
|
| DocumentType |
Standard Practice
|
| Pages |
8
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Current
|
| Supersedes |
1.1This practice covers the essential features of the design and machining, and procedures for stressing, exposing, and inspecting C-ring type of stress-corrosion test specimens. An analysis is given of the state and distribution of stress in the C-ring.
1.2Specific considerations relating to the sampling process and to the selection of appropriate test environments are outside the scope of this practice.
1.3The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard.
1.4This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.5This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
| ASTM G 52 : 2020 | Standard Practice for Exposing and Evaluating Metals and Alloys in Surface Seawater |
| ASTM G 103 : 1997 : R2016 | Standard Practice for Evaluating Stress-Corrosion Cracking Resistance of Low Copper 7XXX Series Al-Zn-Mg-Cu Alloys in Boiling 6 % Sodium Chloride Solution |
| ASTM G 186 : 2005 : R2021 | Standard Test Method for Determining Whether Gas-Leak-Detector Fluid Solutions Can Cause Stress Corrosion Cracking of Brass Alloys |
| ASTM G 111 : 1997 : R2018 | Standard Guide for Corrosion Tests in High Temperature or High Pressure Environment, or Both |
| ASTM F 519 : 2018 | Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments |
| ASTM G 41 : 1990 : R2018 | Standard Practice for Determining Cracking Susceptibility of Metals Exposed Under Stress to a Hot Salt Environment |
| ASTM G 58 : 1985 : R2015 | Standard Practice for Preparation of Stress-Corrosion Test Specimens for Weldments |
| ASTM G 47 : 2020 | Standard Test Method for Determining Susceptibility to Stress-Corrosion Cracking of 2XXX and 7XXX Aluminum Alloy Products |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.