BS EN 10214:1995

Committees responsible
National foreword
Foreword
1. Scope
2. Normative references
3. Definitions
4. Designation
5. Classification of grades and types of delivery
5.1 Steel grades
5.2 Coatings
5.3 Coating finish
5.4 Surface quality
5.5 Surface treatment (temporary surface protection)
6. Requirements
6.1 Manufacturing process
6.2 Selection of properties
6.3 Mechanical properties
6.4 Freedom from coil breaks
6.5 Stretcher strains (low carbon steels for cold
     forming)
6.6 Coating mass
6.7 Adhesion of coating
6.8 Surface condition
6.9 Dimensions, tolerances on dimensions and shape
6.10 Suitability for further processing
7. Testing
7.1 General
7.2 Test units
7.3 Number of tests
7.4 Sampling
7.5 Test methods
7.6 Retests
7.7 Inspection documents
8. Marking
9. Packing
10. Storage and transportation
11. Disputes
12. Information to be supplied by the purchaser
Annex A (normative) Reference method for determination of
the coating mass

Specifies requirements for continuously hot-dip zinc-aluminium alloy coated flat products made of low carbon steels for cold forming or of structural in the thickness less than or equal to 3,0 mm. Covers products that are mainly intended for applications where the protection of the steel base against corrosion is of the greatest importance. Does not apply to: continuously hot-dip zinc coated low carbon steel sheet and strip for cold forming; electrolytically zinc coated steel flat products; continuously organic coated steel flat products; continuously hot-dip aluminium-zinc alloy (AZ) coated steel flat products; continuously organic coated steel flat products.